文献

J-GLOBAL ID：201702214391717624   整理番号：17A0699303

低温浸炭したオーステナイト系ステンレス鋼の熱安定性【Powered by NICT】

Thermal stability of low-temperature-carburized austenitic stainless steel

著者 (6件)： Wang Jun (Department of Materials Science and Engineering, Case Western Reserve University, Cleveland, OH, 44106-7204, USA) ,  Wang Jun (School of Manufacturing Science and Engineering, Sichuan University, Chengdu, 610065, PR China) ,  Li Zhen (Department of Materials Science and Engineering, Case Western Reserve University, Cleveland, OH, 44106-7204, USA) ,  Wang Danqi (Swagelok Center for Surface Analysis of Materials, Case Western Reserve University, Cleveland, OH, 44106-7204, USA) ,  Qiu Shaoyu (The Key Nuclear Fuel and Nuclear Materials Laboratory of China, Nuclear Power Institute of China, Chengdu, 610041, PR China) ,  Ernst Frank (Department of Materials Science and Engineering, Case Western Reserve University, Cleveland, OH, 44106-7204, USA)
資料名： Acta Materialia  (Acta Materialia)
巻： 128  ページ： 235-240  発行年： 2017年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 低温浸炭によるAISI316Lオーステナイト系ステンレス鋼上に形成された「事例」(ハード層)の熱安定性を研究するために,20.7Ms(8か月)の空気中での浸炭試験片を573Kと648K(300および375°C)の間の温度であった。炭素による巨大過飽和にもかかわらず,オーステナイトは炭化物を析出しないなかった。炭素は環境に失われる。炭素は,合金へのより深い拡散し,平坦な炭素分率深さプロフィルをもたらした。平均炭素の深さの温度及び濃度依存性炭素拡散20.7Msの648Kまで曝露二重約を仮定しこれは現実的にシミュレートした。表面近傍の炭素画分は,単に適度に減少し,特に材料は,環境からの炭素を同化する。従って,機械的性質と耐食性に及ぼす低温浸炭の有益な効果は,このような長期熱曝露中保持され,650K以下の温度で低温浸炭した部品の対応する寿命を意味しているCopyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 濃度依存性 ,  炭化物 ,  *低温 ,  機械的性質 ,  炭素 ,  合金 ,  *オーステナイト系ステンレス鋼 ,  耐食性 ,  過飽和 ,  深さプロフィル ,  *熱安定性 ,  *オーステナイト
準シソーラス用語： 高温曝露 ,  AISI316L , 【Automatic Indexing@JST】

著者キーワード (6件)： 低温浸炭 ,  熱曝露 ,  炭素拡散 ,  炭素画分の深さプロファイル ,  走査Augerマイクロプローブ ,  硬度深さプロフィル

分類 (2件)： 表面硬化熱処理  (WC03030E) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： 低温 ,  浸炭 ,  オーステナイト系ステンレス鋼 ,  熱安定性