双峰泡孔構造を有する架橋ポリエチレン発泡材料の調製【JST・京大機械翻訳】

Preparation of Cross-linked Polyethylene Foam with Bi-modalcells Structure

著者 (7件)： Wang Zhanjia (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Qu Zhongjie (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Chen Peng (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Cui Xiaoli (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Xu Guozhi (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Wang Xiangdong (School of Materials and Mechanical Engineering, Beijing Technology and Business University) ,  Zhou Hongfu (School of Materials and Mechanical Engineering, Beijing Technology and Business University)
資料名： Suliao Gongye  (Suliao Gongye)
巻： 44  号： 10  ページ： 104-108  発行年： 2016年 
JST資料番号： C2208A  ISSN： 1005-5770  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 高密度ポリエチレン(HDPE)と架橋剤ジクミルペルオキシド(DCP)をトルク中で溶融混合し,架橋ポリエチレンを調製した。HDPEの架橋前後のレオロジー特性,ゲル含量,溶融および結晶化挙動を,トルク曲線,ゲル含量測定および示差走査熱量測定(DSC)によって研究した。超臨界二酸化炭素を物理的発泡剤として用いて,架橋HDPEを冷却し,そして,圧力降下剤として使用し,走査型電子顕微鏡(SEM)を用いて,二重の形成に及ぼす最初の圧力降下の影響を観察し,そして,体およびとのサイズ分布を,統計的方法によって,統計的に解析した。最後に,発泡試料の見かけの密度を密度平衡法により測定した。その結果,DCPの添加によりHDPEの架橋が起こり,いくつかの網状構造が形成されることが判明した。一次圧力が4MPAに低下すると,材料の形成は理想的である。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *XLPE ,  圧力損失 ,  高密度ポリエチレン ,  *起泡 ,  示差走査熱量測定 ,  走査電子顕微鏡 ,  トルク ,  ゲル ,  *気泡 ,  ネットワーク構造 ,  発泡剤 ,  超臨界二酸化炭素
準シソーラス用語： サイズ分布 ,  レオロジー特性 ,  *発泡材料 , 【Automatic Indexing@JST】

著者キーワード (4件)： High Density Polyethylene ,  Bi-modal Cell Structure ,  Supercritical Carbon Dioxide ,  Synergy between Cooling and Depressurization

分類 (2件)： 高分子固体の構造と形態学  (CG02022M) ,  高分子固体の物理的性質  (CG02024U)

タイトルに関連する用語 (4件)： 泡 ,  架橋ポリエチレン ,  発泡材料 ,  調製