混合硫化物・酸化物鉛及び亜鉛鉱石からのよく整列したZnOナノロッドアレイの合成【Powered by NICT】

Synthesis of well-aligned ZnO nanorod arrays from mixed sulfide-oxide lead and zinc ore

著者 (5件)： Jia Nannan (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Wang Xiaofei (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Wang Hui-gang (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Zhang Mei (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, PR China) ,  Guo Min (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 16  ページ： 18459-18465  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 混合した酸化硫化鉄鉛および亜鉛鉱石からの亜鉛の回収の新規プロセスを,本報で提示した。法の様なZnO種層を事前に被覆したFTO基板上のZnOナノロッドアレイ(ZNRA)を,沈殿と水熱合成を含む酸化性アンモニア浸出プロセスと二段階過程を経て混合鉱石から成功裏に合成した。XRD,SEMおよびUV-vis分光光度計分析によるキャラクタリゼーションの結果から,調製したままのZNRAは,良く整列した,大規模,FTO基板に垂直であり,3.03eVのバンドギャップエネルギーを持つことを示した。XPS解析から,作成したZNRAは少量の炭素をドープし,特に他の不純物を含むFe及びPbしなかったことを示した。全亜鉛抽出は酸化性アンモニア浸出プロセスと析出プロセス後92.4%に達した。亜鉛製造における従来の精製プロセスの除去は効率的で選択的な酸化性アンモニア浸出プロセスによって達成された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 硫化鉄 ,  キャラクタリゼーション ,  水熱合成 ,  *酸化亜鉛 ,  不純物 ,  *鉱石 ,  *鉛 ,  アンモニア ,  X線回折 ,  *亜鉛 ,  沈殿 ,  *亜鉛鉱 ,  ドーピング
準シソーラス用語： バンドギャップエネルギー ,  *ナノロッドアレイ , 【Automatic Indexing@JST】

著者キーワード (3件)： 混合硫化物・酸化物鉛及び亜鉛鉱石 ,  酸化アンモニア浸出 ,  ZnOナノロッドアレイ

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (7件)： 硫化物 ,  酸化物 ,  鉛 ,  亜鉛鉱石 ,  整列 ,  ZnOナノロッド ,  アレイ