低炭素鋼のI&Q&P処理後の微細構造と性質に及ぼすMN分配時間の影響を研究した。【JST・京大機械翻訳】

Effect of Mn Partitioning Time on Microstructure and Properties of Low-carbon Steel with I&Q&P Treatment

著者 (6件)： Tian Yaqiang (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology) ,  Li Ran (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology) ,  Song Jinying (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology) ,  Wei Yingli (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology) ,  Dai Xin (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology) ,  Chen Liansheng (Hebei Key Laboratory of Modem Metallurgy Technology, North China University of Science and Technology)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 16  ページ： 161-164  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： I&Q&P(二相領域焼なまし+焼入+分配)処理により,電界放出走査型電子顕微鏡(SEM)とX線回折(XRD)を用いて,複合材料を特性化した。低炭素鋼中のMN元素の分配挙動及びその分布プロセスパラメータがI&Q&P処理後の組織と性能に与える影響を研究した。結果は以下を示す。I&Q&Pプロセスによって処理した後に,I&QプロセスにおけるMN分配効果は除去されず,室温では,マルテンサイト,残留オーステナイト,および少量の塊状マルテンサイトが観察された。同じ分配温度において,残留オーステナイトの含有量は,分配時間の延長とともに,最初に増加し,次に減少した。材料の引張強さは低下傾向を示した。伸びの変化は残留オーステナイト量の変化傾向と一致した。その総合的性能は,29046.65MPA%に達することができた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 引張強さ ,  走査電子顕微鏡 ,  プロセスパラメータ ,  焼なまし ,  伸び ,  X線回折 ,  マルテンサイト ,  焼入 ,  複合材料 ,  *低炭素鋼 ,  残留オーステナイト ,  電界放出 ,  キャラクタリゼーション ,  *微細構造

著者キーワード (5件)： Mn partitioning parameters ,  I&Q&P (intercritical annealing & quenching & partitioning) process ,  retained austenite ,  elongation ,  tensile strength