MG-12AL-1ZN合金の微細構造と性質に及ぼす均質化焼鈍の影響を研究した。【JST・京大機械翻訳】

Effects of Homogenizing Annealing on Microstructure and Properties of Mg-12Al-1Zn Alloy

著者 (5件)： Han Xi (Department of Chemical Engineering and Modern Material, Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources, Shangluo University) ,  Yang Jungang (Department of Materials Science and Engineering, Xi’an University of Technology) ,  He Bingkui (Department of Materials Science and Engineering, Xi’an University of Technology) ,  Zhou Chunsheng (Department of Chemical Engineering and Modern Material, Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources, Shangluo University) ,  Liu Yanfeng (Department of Chemical Engineering and Modern Material, Shaanxi Key Laboratory of Tailings Comprehensive Utilization of Resources, Shangluo University)
資料名： Rejiagong Gongyi  (Rejiagong Gongyi)
巻： 45  号： 16  ページ： 239-241  発行年： 2016年 
JST資料番号： C2487A  ISSN： 1001-3814  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： MG-12AL-LZN合金の均質化焼鈍後のミクロ組織と性質を研究した。結果は以下を示す。Β-MG_(17)AL_(12)相の析出は420°Cで24時間の均質化の後,Β-MG_(17)AL_(12)相の析出によって増加した。冷却速度が0.0201K/Sのときには,平均ラメラ間隔は冷却速度の低下とともに増加し,少量の溶解があった。均質化焼鈍後に,合金の硬度は,鋳造速度の増加とともに増加し,そして,冷却速度の低下とともに,減少し,そして,冷却速度が0.0201K/Sのとき,最大値は,87.7HBに達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 層間隔 ,  *均質化 ,  硬度 ,  *焼なまし ,  鋳込速度 ,  *合金 ,  冷却速度 ,  微細構造

著者キーワード (4件)： Mg-12Al-lZn magnesium alloy ,  homogenizing annealing ,  β-Mg_(17)Al_(12) phase ,  hardness