時効処理中の2219アルミニウム合金のミクロ組織と性質に及ぼす予変形の影響【Powered by NICT】

Effect of pre-deformation on the microstructures and properties of 2219 aluminum alloy during aging treatment

著者 (8件)： Lu Yalin (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, Changzhou, China) ,  Lu Yalin (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Wang Jian (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Li Xingcheng (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, Changzhou, China) ,  Chen Yi (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, Changzhou, China) ,  Zhou Dongshuai (Key Construction Laboratory of Green Forming and Equipment from Jiangsu Province, Changzhou, China) ,  Zhou Gang (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China) ,  Xu Wenting (School of Materials Engineering, Jiangsu University of Technology, Changzhou, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 699  ページ： 1140-1145  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 時効処理中の2219アルミニウム合金の予変形度の微細構造と特性の変化を調べた。結果は,予変形は,同様にαマトリックスにおける分散分布を有するち密で小さい沈殿θ′相の形成をもたらし,これは予備変形サンプルの強度の増強をもたらすマトリックス中の転位密度の増加をもたらすことを明らかにした。も4.19%予備変形試料の強度は,2.88%予備変形試料と比較して急激なわずかに減少を示すことが観測され,これはマトリックス中の予変形により形成された転位セルの大きな量のために不均一分布したθ′析出物の形成に起因する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 転位密度 ,  *アルミニウム合金 ,  析出物 ,  微細構造 ,  沈殿
準シソーラス用語： 不均一分布 , 【Automatic Indexing@JST】

著者キーワード (4件)： 2219アルミニウム合金 ,  予変形 ,  Microstructures ,  機械的性質

分類 (1件)： 組織的硬化現象  (WB01020C)

タイトルに関連する用語 (4件)： 時効処理 ,  アルミニウム合金 ,  ミクロ組織 ,  性質