酸カルシウム/グラフェン複合核剤の調製と応用研究【JST・京大機械翻訳】

Preparation and Application of Calcium Pimelate/Graphene Compound Nucleating Agent for Polypropylene

著者 (4件)： Liu Bao (School of Chemistry and Biological Engineering,Changsha University of Science and Technology, Hunan Province Key Laboratory of Materials Protection for Electric Power and Transportation) ,  Zhang Yuefei (School of Chemistry and Biological Engineering,Changsha University of Science and Technology, Hunan Province Key Laboratory of Materials Protection for Electric Power and Transportation) ,  Jiang Youzhou (School of Chemistry and Biological Engineering,Changsha University of Science and Technology, Hunan Province Key Laboratory of Materials Protection for Electric Power and Transportation) ,  Wang Chunyao (School of Chemistry and Biological Engineering,Changsha University of Science and Technology, Hunan Province Key Laboratory of Materials Protection for Electric Power and Transportation)
資料名： Suliao Gongye  (Suliao Gongye)
巻： 44  号： 9  ページ： 117-119  発行年： 2016年 
JST資料番号： C2208A  ISSN： 1005-5770  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 新しい高効率のポリプロピレン(酸)/酸(グラフェン)複合核剤を調製した。FOURIER変換赤外分光分析(FTIR)を用いてCAHA/GRAの複合構造を測定し,示差走査熱量測定(DSC)を用いてPP/PP複合材料の結晶化と融解挙動を試験した。結果は,酸とグラフェンの間には単純な機械的混合ではなく,化学的結合によってPP中のCAHA/GRAの分散性が改善されることを示した。PPの結晶化温度はPPの核形成剤の添加により明らかに改善され,複合材料核剤の添加量が0.2%(質量分率)のとき,PPの結晶化温度はブランクPPの121°Cから126°Cに上昇した。同時に,核形成ポリプロピレンには相当量のΑ結晶相とΒ結晶相が出現し,平衡PPの剛性と靱性に良好な影響を与えた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  示差走査熱量測定 ,  化学結合 ,  複合材料 ,  結晶化 ,  分散度 ,  *グラフェン ,  剛性 ,  晶出温度 ,  複合構造 ,  靱性 ,  質量分率 ,  機械的性質
準シソーラス用語： 結晶相 ,  *核剤 ,  高効率 , 【Automatic Indexing@JST】

著者キーワード (4件)： Compound Nucleating Agent ,  Calcium Pimelate ,  Graphene ,  Polypropylene