MWCNTはスパークプラズマ焼結によるτMnAlナノ複合材料磁石を強化【Powered by NICT】

MWCNT reinforced τ-Mn-Al nanocomposite magnets through spark plasma sintering

著者 (5件)： Saravanan P. (Defence Metallurgical Research Laboratory, Hyderabad 500058, India) ,  Hsu Jen-Hwa (Department of Physics, National Taiwan University, Taipei 106, Taiwan) ,  Vinod V.T.P. (Institute for Nanomaterials, Advanced Technologies and Innovation, Department of Natural Sciences, Technical University of Liberec, Studentska 1402/2, Liberec 1 461 17, Czech Republic) ,  Cernik Miroslav (Institute for Nanomaterials, Advanced Technologies and Innovation, Department of Natural Sciences, Technical University of Liberec, Studentska 1402/2, Liberec 1 461 17, Czech Republic) ,  Kamat S.V. (Defence Metallurgical Research Laboratory, Hyderabad 500058, India)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 364-371  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： τ相の結晶粒微細化と安定化を介して希土類自由Mn_56Al_44永久磁石の性能を増強するための多層カーボンナノチューブ(MWCNT)とスパークプラズマ焼結(SPS)の両方の固有の利点を利用した。残留磁化,保磁力とエネルギー積値の良好な組合せ:42.5emu/g,3.22kOe,1.92MGOe;45.6emu/g,3.64kOe,2.26MGOeはMWCNTの1.5および2wt%を添加したSPSしたMn-Al磁石の各々に対して達成された。SPSしたMn Al/MWCNTナノ複合材料磁石で観察された保磁力増大は磁壁ピン止めから生じ,粒界で破壊したナノチューブと非晶質炭素質材料の形でMWCNTsの析出の結果と仮定されている。が,以上のことを確認するための本質的なより詳細な研究,この戦略はSPSプロセスを用いた簡単な方法で高性能希土類自由Mn-Al永久磁石を製造するための新しい基礎を提供する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ピン止め ,  炭素材 ,  保磁力 ,  *放電プラズマ焼結 ,  結晶粒界 ,  結晶粒微細化 ,  *ナノ複合材料 ,  ナノチューブ ,  永久磁石 ,  磁壁 ,  *磁石 ,  残留磁化 ,  *多層カーボンナノチューブ
準シソーラス用語： エネルギー積 ,  τ相 , 【Automatic Indexing@JST】

著者キーワード (5件)： 希土類フリー永久磁石 ,  多層カーボンナノチューブ ,  Mn-Al磁石 ,  高エネルギーボールミル粉砕 ,  スパークプラズマ焼結

分類 (2件)： 圧粉,焼結  (WC02030X) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： MWCNT ,  スパークプラズマ焼結 ,  ナノ複合材料 ,  磁石 ,  強化