MOSI_2の耐酸化性に及ぼす長石釉の影響を研究した。【JST・京大機械翻訳】

Influence of Feldspar Glaze on the Oxidation Resistance of MoSi_2 at Low Temperature

著者 (5件)： Li Xiulin (School of Materials Science and Engineering, Central South University, Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education) ,  Yi Danqing (School of Materials Science and Engineering, Central South University, Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education) ,  Liu Huiqun (School of Materials Science and Engineering, Central South University, Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education) ,  Wang Bin (School of Materials Science and Engineering, Central South University, Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education) ,  Ren Yan (School of Materials Science and Engineering, Central South University)
資料名： Taoci Xuebao  (Taoci Xuebao)
巻： 37  号： 2  ページ： 140-146  発行年： 2016年 
JST資料番号： C3005A  ISSN： 2095-784X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 原料としてカオリン,長石,石灰石,石英を用いて,9つの釉薬を,L_9(34)直交実験によって設計し,そして,その微細構造を,電界放出走査型電子顕微鏡によって観察した。MOSI_2の耐酸化性に及ぼす明確にの影響を研究した。結果は以下を示す。焼成温度の上昇とともに,明確にはより容易になり,表面の欠陥は減少し,1250°Cまでの温度上昇とともに,表面の欠陥は明らかに減少し,そして,最適焼結温度は1250°Cであり,そして,表面の欠陥は,保持時間の延長とともに減少した。空気中で500°Cで酸化試験を行った結果,未塗覆釉のMOSI_2の酸化重量増加はほぼ直線的に増加し,塗布の厚さが4.8~20.8ΜMのMOSI_2の質量はほとんど変化しないことが分かった。これらの結果は,エナメルがMOSI_2の低温酸化抵抗を明らかに改善できることを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 石英 ,  走査電子顕微鏡 ,  *釉薬 ,  保持時間 ,  カオリン ,  *酸化 ,  *耐酸化性 ,  昇温 ,  石灰石 ,  塗布 ,  電界放出 ,  *長石
準シソーラス用語： 低温酸化 ,  焼結温度 ,  焼成温度 , 【Automatic Indexing@JST】

著者キーワード (4件)： glaze ,  microstructure ,  firing process ,  oxidation resistance