Sm(Fe,Si)-9C/α-Feナノ複合材料磁石の構造と磁気的性質【Powered by NICT】

Structure and magnetic properties of Sm(Fe,Si)₉C/α-Fe nanocomposite magnets

著者 (7件)： Bez Riadh (CMTR, ICMPE, UMR7182, CNRS, Universite Paris Est, 2-8 rue Henri Dunant, F-94320, Thiais, France) ,  Bez Riadh (LMOP LR99ES17, Faculte des Sciences de Tunis, Universite de Tunis El Manar, 2092, Tunis, Tunisia) ,  Zehani Karim (CMTR, ICMPE, UMR7182, CNRS, Universite Paris Est, 2-8 rue Henri Dunant, F-94320, Thiais, France) ,  Batuk Maria (EMAT, University of Antwerp, B-2020, Antwerp, Belgium) ,  Van Tendeloo Gustaaf (EMAT, University of Antwerp, B-2020, Antwerp, Belgium) ,  Mliki Najeh (LMOP LR99ES17, Faculte des Sciences de Tunis, Universite de Tunis El Manar, 2092, Tunis, Tunisia) ,  Bessais Lotfi (CMTR, ICMPE, UMR7182, CNRS, Universite Paris Est, 2-8 rue Henri Dunant, F-94320, Thiais, France)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 810-817  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： SmFe_8 0.75Si_0-0.25C/α-Feナノ複合材料を成功裏に高エネルギーミリングを用いて合成し,続いて750°Cでアニールした。これらの化合物の結晶構造を粉末X線回折データを用いたRietveld法によって特性化した。Smの濃度を増加させることによって,著者等はα-Fe相の量の減少を観察した。試料の形態を,走査及び透過型電子顕微鏡により決定した。平均粒径は約20nmであった。磁気特性を室温と10Kで調べた。強磁性挙動は両温度でのすべての試料で観察された。軟磁性相α-Feの増加は,磁化の増加と保磁力の減少を誘導した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 強磁性 ,  結晶構造 ,  *サマリウム ,  *磁石 ,  透過型電子顕微鏡 ,  *磁気的性質 ,  磁化 ,  Rietveld法 ,  保磁力 ,  キャラクタリゼーション ,  *ナノ複合材料
準シソーラス用語： 軟磁性 ,  平均粒子径 ,  粉末X線回折 ,  高エネルギー , 【Automatic Indexing@JST】

著者キーワード (3件)： ナノ複合材料 ,  構造特性 ,  磁気的性質

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： Sm ,  Fe ,  Si ,  ナノ複合材料 ,  磁石 ,  磁気的性質