PA//SMAブレンドの調製と性能研究【JST・京大機械翻訳】

Preparation and Performance of PA1012/SMA blends

著者 (6件)： Chen Xuejin (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology) ,  Lyu Guangchao (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology) ,  Xu Yanbin (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology) ,  Liu Bairan (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology) ,  Wu Guangfeng (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology) ,  Zhang Huixuan (Engineering Research Center of Synthetic Resin and Special Fiber of Ministry of Education,Changchun University of Technology)
資料名： Suliao Gongye  (Suliao Gongye)
巻： 44  号： 10  ページ： 26-29  発行年： 2016年 
JST資料番号： C2208A  ISSN： 1005-5770  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ナイロン1012(PA1012)/スチレン-無水マレイン酸(SMA)ブレンドを二軸押出法により調製し,PA含有量がPA//SMAブレンドの機械的性質に及ぼす影響を調べた。走査型電子顕微鏡(SEM)を用いて,PA1010/SMAブレンドの微細構造を研究した。その結果,SMAの添加により,ブレンドの衝撃強さは,最初に増加し,次に減少し,そして,ブレンドの引張強さおよび弾性率は,減少した。SMA含有量が0.5%のとき,PA1010/SMAブレンドの衝撃強さは298J/Mに達し,靭性は破壊され,機械的性質は優れていた。PA1010/SMAブレンドの結晶化温度は10°Cよりも高く,結晶化に有利であった。SEM観察から,SMA分散相粒子の含有量が増加するにつれて,PA1012マトリックス中での分散はより均一であり,均一になることがわかった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *衝撃強さ ,  晶出温度 ,  機械的性質 ,  引張強さ ,  結晶化 ,  走査電子顕微鏡 ,  弾性係数 ,  微細構造 ,  靱性 ,  二軸