超高強度アルミニウム合金の機械的性質と耐食性に及ぼすT76時効の影響を研究した。【JST・京大機械翻訳】

Effect of T76 temper on mechanical properties and corrosion resistance of an ultra-high strength aluminum alloy

著者 (6件)： Yang Fan (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University) ,  Xu Xiaojing (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University) ,  Deng Pingan (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University) ,  Zhu Jinxin (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University) ,  Ding Qing (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University) ,  Wang Chengsong (Institute of Advanced Manufacturing and Modern Equipment Technology Engineering, Jiangsu University)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 11  ページ： 40-44  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 硬度と電気伝導率試験,引張試験,粒界腐食,剥離腐食試験,走査型電子顕微鏡(SEM)観察,およびXRD分析を採用した。AL-11.54ZN-3.51MG-2.26CU-0.24ZR-0.0025SR合金の前処理(250°C×24H+300°C×6H+350°C×6H+400°C×6H)の前処理(450°C×5H+153°C×16H)後の引張強さ,硬度,電気伝導率,粒界腐食および剥離腐食性能を研究した。その結果,T6時効後の合金の硬度および強度は,T6時効後のそれらと比較して,明らかに減少し,そして,それは,それぞれ,9.59%および12.46%減少したが,依然として,高レベルを維持した。それらの電気伝導率と伸びは,それぞれ,19.64%と28.13%増加した。剥離腐食はEBレベルからEAレベルまで上昇した。粒界腐食深さは147.5ΜMから113.11ΜMに変化した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *時効 ,  伸び ,  粒界腐食 ,  *合金 ,  硬度 ,  機械的性質 ,  前処理 ,  電気伝導率 ,  走査電子顕微鏡 ,  *耐食性 ,  引張強さ ,  引張試験
準シソーラス用語： 剥離腐食 , 【Automatic Indexing@JST】

著者キーワード (4件)： T76 temper ,  mechanical property ,  inter-granular corrosion ,  exfoliation corrosion

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 高強度アルミニウム合金 ,  機械的性質 ,  耐食性 ,  時効 ,  研究