Effect of Ultrasonic Peening on Very High Cycle Fatigue Behavior of Friction Stir Welded Joint in Aluminum Alloy

著者 (5件)： Li Xue (College of Architecture and Civil Engineering, Xihua University) ,  He Chao (School of Architecture and Civil Engineering, Chengdu University, Failure Mechanics, Engineering Disaster Prevention and Mitigation Key Laboratory of Sichuan Province) ,  Yang Kun (Failure Mechanics, Engineering Disaster Prevention and Mitigation Key Laboratory of Sichuan Province, Sichuan University) ,  Liu Yongjie (Failure Mechanics, Engineering Disaster Prevention and Mitigation Key Laboratory of Sichuan Province, Sichuan University) ,  Wang Qingyuan (Failure Mechanics, Engineering Disaster Prevention and Mitigation Key Laboratory of Sichuan Province, Sichuan University)
資料名： Shiyan Lixue  (Shiyan Lixue)
巻： 31  号： 6  ページ： 809-818  発行年： 2016年 
JST資料番号： C2470A  ISSN： 1001-4888  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 2つのアルミニウム合金(AA6061とAA7075)の摩擦撹拌溶接の疲労挙動に及ぼす超音波衝撃処理の影響を,超音波疲労試験によって研究した。微細構造,微小硬さ,およびX線回折法を用いて,表面処理技術の特性を研究した。結果により,超音波衝撃処理は,接合部表面上に強化層を形成することができ,そして,疲労亀裂を,試験片の表面に,内部に移動させることができた。アルミニウム合金AA6061に対して,継手の疲れ強さは,処理前後でほとんど差がなかったが,AA7075継手の疲労寿命は,著しく増加した。最後に,疲労亀裂発生の特性,表面強化層,および残留応力が疲労強度に及ぼす影響機構を分析した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 疲れ試験 ,  *摩擦撹拌溶接 ,  残留応力 ,  疲れ強さ ,  *超音波 ,  疲れ寿命 ,  微小硬さ ,  *衝撃 ,  疲れ亀裂 ,  *アルミニウム合金 ,  X線回折分析 ,  試験片
準シソーラス用語： 超音波衝撃処理 ,  AA7075 ,  AA6061 , 【Automatic Indexing@JST】

著者キーワード (5件)： friction stir welding ,  very high cycle fatigue ,  ultrasonic peening treatment(UPT) ,  fatigue crack initiation ,  Aluminum alloy