ポリ(乳酸)複合材料の加水分解挙動に及ぼす強化粒子の影響【Powered by NICT】

Effect of reinforcing particles on hydrolytic degradation behavior of poly (lactic acid) composites

著者 (5件)： Li Mei-Xian (Department of Mechanical and Aerospace Engineering, Seoul National University, Seoul 151-744, South Korea) ,  Kim Sung-Ha (Department of Mechanical and Materials Technology, Fluid Machinery & Systems Company, Ebara Corporation, Fujisawa-shi, Kanagawa 251-8501, Japan) ,  Choi Sung-Woong (Department of Extreme Energy Systems, Korea Institute of Machinery and Materials, Gimhae-si, Gyeongsangnam-do 641-842, South Korea) ,  Goda Koichi (Department of Mechanical Engineering, Yamaguchi University, Tokiwadai 2-16-1, Ube 755-8611, Japan) ,  Lee Woo-Il (Department of Mechanical and Aerospace Engineering, Seoul National University, Seoul 151-744, South Korea)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 96  ページ： 248-254  発行年： 2016年07月01日 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,異なるタイプの粒子(二酸化チタン,多層カーボンナノチューブ,表面処理した多層カーボンナノチューブおよびグラフェンナノプレートレット)で強化されたポリ乳酸(PLA)複合材料の劣化挙動を調べた。試料は押出および射出成形によって調製した。加水分解は水酸化ナトリウム溶液中で試料を浸漬することにより誘導された。粒子は分解挙動に影響するPLAマトリックスの結晶化速度に影響を与えることができる。PLAマトリックスの結晶化速度及び結晶化度を調べるために,示差走査熱量測定およびX線回折測定を採用した。マトリックスの結晶化度を制御するためにアニーリングは種々の時間行った。結果は結晶化速度は,粒子の添加により著しく増加したことを,粒子の最適濃度であることを示した。最もPLA複合材料の分解速度は,純PLAの場合よりも速く,粒子とPLAマトリックス間の界面は完全ではないことを示した。一方,多層カーボンナノチューブで強化したPLAの分解速度は結晶化度の増加のために遅くなった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶度 ,  水酸化ナトリウム ,  *ポリ乳酸 ,  示差走査熱量測定 ,  多層カーボンナノチューブ ,  浸漬 ,  *複合材料 ,  X線回折 ,  界面 ,  晶析速度 ,  *加水分解 ,  焼なまし ,  射出成形
準シソーラス用語： 分解速度 ,  二酸化チタン , 【Automatic Indexing@JST】

著者キーワード (3件)： A粒子強化 ,  B環境劣化 ,  E.熱処理

分類 (2件)： 強化プラスチックの成形  (YH04060J) ,  充填剤,補強材  (YH05030J)

タイトルに関連する用語 (5件)： 乳酸 ,  複合材料 ,  加水分解 ,  挙動 ,  強化