ポリ乳酸/SIO_X薄膜の調製とガスへの透過性と選択性【JST・京大機械翻訳】

Preparation of Poly (L-lactic acid)/SiO_x Film and Its Gas Permeability and Permselectivity

著者 (7件)： Song Shuxin (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Liang Min (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Wang Yu (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Liu Linlin (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Zhang Yuqin (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Qi Xiaojing (College of Food Science and Engineering, Inner Mongolia Agricultural University) ,  Dong Tungalag (College of Food Science and Engineering, Inner Mongolia Agricultural University)
資料名： Gaofenzi Cailiao Kexue yu Gongcheng  (Gaofenzi Cailiao Kexue yu Gongcheng)
巻： 32  号： 11  ページ： 135-139  発行年： 2016年 
JST資料番号： C2119A  ISSN： 1000-7555  CODEN： GCKGEI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： プラズマ強化化学気相成長法(PECVD)を用いて,ポリ乳酸(PLLA)薄膜の表面にSIO_X層を堆積させ,ガス透過性と選択性を改善した。赤外分光光度計と透過型電子顕微鏡を用いて,堆積効果と膜透過性を試験した。その結果,PLLA/SIO_X複合膜は,純粋なPLLA膜と比較して,ガス透過性を低下させ,そして,選択性を改善した。O_2,CO_2,N_2,および水蒸気の透過性は,25°Cでの40ΜMのPLLA/SIO_X膜において,それぞれ58.9%,48.6%,および67.8%であった。透過(CO_2/O_2),Α(O_2/N_2),およびΑ(CO_2/N_2)は,それぞれ20.0%,21.8%,および37.5%であった。O_2,CO_2,N_2,および水蒸気の透過性は,25°Cで,それぞれTB.AR%,14.5%,46.7%,および49.5%に減少した。CO_2/O_2,CO_2/N_2およびCO_2/N_2の比率は,それぞれ10.7%,であった%およびTB.AR%増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *透過 ,  化学蒸着 ,  透過型電子顕微鏡 ,  *薄膜 ,  プラズマCVD ,  透気性 ,  複合膜 ,  プラズマ
準シソーラス用語： 膜透過性 ,  *透過性 , 【Automatic Indexing@JST】

著者キーワード (5件)： poly (L-lactic acid) ,  plasma enhanced chemical vapour deposition ,  SiO_x coatings ,  gas permeability ,  gas permselectivity

分類 (3件)： 膜分離  (XD02120Z) ,  無機重合体  (YH07140R) ,  分析機器  (CC02020S)

タイトルに関連する用語 (5件)： ポリ乳酸 ,  薄膜 ,  調製 ,  透過性 ,  選択性