MoS_2のアルギン酸ナトリウム支援剥離および高分子ナノ複合体におけるその強化【Powered by NICT】

Sodium alginate-assisted exfoliation of MoS₂ and its reinforcement in polymer nanocomposites

著者 (4件)： Xuan Dandan (College of Chemistry & Chemical Engineering, Anhui University, Anhui Province Key Laboratory of Environment-friendly Polymer Materials, Hefei 230601, China) ,  Zhou Yifeng (College of Chemistry & Chemical Engineering, Anhui University, Anhui Province Key Laboratory of Environment-friendly Polymer Materials, Hefei 230601, China) ,  Nie Wangyan (College of Chemistry & Chemical Engineering, Anhui University, Anhui Province Key Laboratory of Environment-friendly Polymer Materials, Hefei 230601, China) ,  Chen Pengpeng (College of Chemistry & Chemical Engineering, Anhui University, Anhui Province Key Laboratory of Environment-friendly Polymer Materials, Hefei 230601, China)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 155  ページ： 40-48  発行年： 2017年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,二硫化モリブデン(MoS_2)ナノシートを容易にアルギン酸ナトリウム(SA)の助けを借りて水性媒体中でMoS_2の直接剥離によって調製した。透過型電子顕微鏡(TEM),X線回折(XRD)とRamanスペクトルの結果は生MoS_2た数層MoS_2ナノシート(SA MoS_2)への剥離に成功したことを示した。FTIRおよび熱重量分析(TGA)研究は,得られたMoS_2ナノシートは剥離後のSAで改質し,水中の改善された分散が達成されたことを示した。得られたSA MoS_2ナノシートを水溶性高分子SAを強化するために採用した。著明な巨視的な相分離はSA/SA MoS_2膜から検出されなかった。動的機械分析(DMA)の結果は,SAの貯蔵弾性率のほぼ9倍の増強はわずか0.5wt%SA MoS_2の導入で達成され,SAの熱安定性も熱重量分析TGA結果によればSA MoS_2の添加により改善することを見出したことを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 相分離 ,  Ramanスペクトル ,  *高分子 ,  動的機械分析 ,  媒質 ,  熱重量分析 ,  *ナノ複合材料 ,  動弾性係数 ,  透過型電子顕微鏡 ,  水溶性高分子 ,  熱安定性 ,  X線回折 ,  ナノシート
準シソーラス用語： 二硫化モリブデン ,  *アルギン酸ナトリウム , 【Automatic Indexing@JST】

著者キーワード (4件)： 二硫化モリブデン ,  アルギン酸ナトリウム ,  Nanocomposites ,  熱的及び機械的性質

分類 (2件)： 多糖類  (CF10054P) ,  高分子固体のその他の性質  (CG02025L)

タイトルに関連する用語 (5件)： アルギン酸ナトリウム ,  支援 ,  高分子 ,  ナノ複合体 ,  強化