三元ニッケル合金上のナノ双晶面の作製への新しいアプローチ【Powered by NICT】

A novel approach to fabricating a nanotwinned surface on a ternary nickel alloy

著者 (14件)： Zhang Zhenyu (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China) ,  Zhang Zhenyu (Changzhou Institute of Dalian University of Technology, Changzhou 213164, China) ,  Zhang Zhenyu (State Key Laboratory of Tribology, Tsinghua University, Beijing 100084, China) ,  Wang Bo (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China) ,  Wang Bo (Key Laboratory of Marine Materials and Related Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Huang Siling (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China) ,  Wen Bin (State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China) ,  Yang Song (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China) ,  Zhang Bi (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China) ,  Zhang Bi (Department of Mechanical Engineering, University of Connecticut, Storrs, CT 06269, USA) ,  Lin Cheng-Te (Key Laboratory of Marine Materials and Related Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Jiang Nan (Key Laboratory of Marine Materials and Related Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China) ,  Jin Zhongmin (School of Mechanical Engineering, University of Leeds, Leeds LS2 9JT, UK) ,  Guo Dongming (Key Laboratory for Precision and Non-Traditional Machining Technology, Ministry of Education, Dalian University of Technology, Dalian 116024, China)
資料名： Materials & Design  (Materials & Design)
巻： 106  ページ： 313-320  発行年： 2016年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 変形ナノ双晶は三元ニッケル(Ni)合金の単結晶上に分子動力学(MD)を用いて行った。一般化埋込み原子法(EAM)ポテンシャル関数を三元Ni合金が得られた。臨界双晶化応力は4.48GPa,MDシミュレーションにより計算した。非双晶,復元と再生ナノ双晶は除荷過程時に起こり,延性の残りに寄与した。MDシミュレーションによれば,室温でのナノインデンテーションを用いてナノ双晶化した表面を作製するための新しい手法を提案した。は以前の報告であり,高温,高圧または化学試薬を用いたとは異なっている。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノインデンテーション ,  *双晶 ,  単結晶 ,  高温 ,  臨界 ,  除荷 ,  分子動力学 ,  高圧 ,  *ニッケル合金 ,  延性
準シソーラス用語： 双晶化 ,  ポテンシャル関数 ,  埋込み原子法 ,  *ナノ双晶 , 【Automatic Indexing@JST】

著者キーワード (5件)： 分子動力学 ,  ナノ双晶化 ,  ナノ双晶化表面 ,  透過型電子顕微鏡観察 ,  三元ニッケル合金