金属有機分解により作製したマンガンをドープしたNa_0 5Bi_0 5TiO_3ナノ結晶薄膜の強誘電及び誘電特性:単層厚さに依存した研究【Powered by NICT】

Ferroelectric and dielectric properties of manganese-doped Na_0.5Bi_0.5TiO₃ nanocrystalline thin films prepared by metal organic decomposition: A single-layer thickness-dependent study

著者 (5件)： Yang Changhong (School of Material Science and Engineering, University of Jinan, Jinan 250022, PR China) ,  Yang Changhong (Shandong Provincial Key Laboratory of Preparation and Measurement of Building Materials, University of Jinan, Jinan 250022, PR China) ,  Lv Panpan (School of Material Science and Engineering, University of Jinan, Jinan 250022, PR China) ,  Song Jiahong (School of Material Science and Engineering, University of Jinan, Jinan 250022, PR China) ,  Feng Chao (School of Material Science and Engineering, University of Jinan, Jinan 250022, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 14  ページ： 15338-15342  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 15 45nm/l~単層厚さを持つ2at%マンガンをドープしたNa_0 5Bi_0 5TiO_3(NBTMn)薄膜を有機金属分解法及びスピンコーティング法により酸化インジウムスズ/ガラス基板上に堆積した。結晶構造,表面形態,絶縁能力,強誘電及び誘電特性に及ぼす単層厚さの影響を主に調べた。他の膜と比較して,単層厚さ30nm/lのNBTMn膜は(110)優先配向と緻密な構造を示した。また,優先配向と低い漏れ電流密度による38μC/cm~2の大きな残留分極(P)強化された強誘電性を示した。30nm/lとNBTMnに対して39%の高い誘電可調性を測定印加電圧と周波数を変化させることにより観測できた。これらの結果は,適切な層の厚さがNBTMn薄膜の電気的性能を改善するのに有益であることを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 酸化インジウムスズ ,  *ドーピング ,  優先配向 ,  結晶構造 ,  *誘電性 ,  残留分極 ,  スピンコーティング ,  *マンガン ,  *単一層 ,  強誘電性 ,  印加電圧 ,  表面形態 ,  ガラス基板
準シソーラス用語： 漏れ電流密度 ,  MOD法 , 【Automatic Indexing@JST】

著者キーワード (4件)： 薄膜 ,  単層厚さ ,  結晶構造 ,  電気的性質

分類 (2件)： 酸化物薄膜  (BK14050P) ,  強誘電体,反強誘電体,強弾性  (BM05030B)

タイトルに関連する用語 (9件)： 有機分解 ,  作製 ,  マンガン ,  ドープ ,  ナノ結晶薄膜 ,  誘電特性 ,  単層 ,  厚さ ,  研究