Ca-Ag金属ガラスの化学的脱合金化により作製したナノ多孔質銀の脱合金化条件と粗大化挙動の間の相関【Powered by NICT】

Correlation between dealloying conditions and coarsening behaviors of nanoporous silver produced by chemical dealloying of Ca-Ag metallic glass

著者 (4件)： Jin Yu (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Li Ran (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Zuo Lei (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Zhang Tao (Key Laboratory of Aerospace Materials and Performance (Ministry of Education), School of Materials Science and Engineering, Beihang University, Beijing 100191, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 1600-1609  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 調整可能なリガメントサイズのナノ多孔性銀(NPS)は,純水と水性HCl溶液中での脱合金Ag_60 5Ca_39 5二元金属ガラスで調製した。NPSの形態に及ぼす種々の脱合金化パラメータの影響をガラス状前駆体から生成したNPSの粗粒挙動を明らかにするために,包括的に評価した。得られたNPSのリガメントサイズは表面拡散モデルを用いて定量的に相関させることができる。さらに,小さいリガメントサイズとより高い表面積をもつ脱合金したままのNPSは,より高い電気化学的触媒活性を示した。結果は実験パラメータを制御することによって望ましい形態と性能を持つNPSを合成するための重要な洞察を提供した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 触媒活性 ,  純水 ,  表面拡散 ,  塩酸 ,  表面積 ,  *銀 ,  *ガラス ,  電気化学 ,  前駆体 ,  *金属ガラス
準シソーラス用語： *ナノポーラス ,  *脱合金 , 【Automatic Indexing@JST】

著者キーワード (4件)： 金属ガラス ,  ナノ多孔性 ,  脱合金化 ,  電極触媒酸化