模擬一次冷却水中の308Lステンレス鋼溶接金属中の環境助長亀裂成長【Powered by NICT】

Environmentally assisted crack growth in 308L stainless steel weld metal in simulated primary water

著者 (6件)： Dong Lijin (Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang City 110819, China) ,  Dong Lijin (Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang City 110016, China) ,  Han En-Hou (Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang City 110016, China) ,  Peng Qunjia (Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang City 110016, China) ,  Ke Wei (Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang City 110016, China) ,  Wang Lei (Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang City 110819, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 117  ページ： 1-10  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 模擬一次水中の308Lステンレス鋼溶接金属の環境助長亀裂成長挙動を調べた。結果は溶接金属中の超低応力腐食亀裂成長を示した。しかし,疲れ亀裂成長の明らかな環境加速が観察され,これは,より積極的な水化学と穏やかな繰返し荷重条件により増加した。さらに,308L溶接金属の環境疲労亀裂成長速度は,同じ環境と負荷状態の下で304および316ステンレス鋼のそれよりも低かった。これはδフェライト相による亀裂成長の遅延に起因した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 応力腐食 ,  応力腐食割れ ,  疲れ亀裂成長速度 ,  *ステンレス鋼 ,  *溶接 ,  疲れ亀裂成長 ,  δフェライト ,  *溶接金属 ,  水化学 ,  *亀裂伝搬 ,  繰返し荷重 ,  *冷却水

著者キーワード (5件)： A.ステンレス鋼 ,  B SEM ,  C.腐食疲労 ,  C.応力腐食 ,  C.溶接