J-GLOBAL ID：201702232128996337   整理番号：17A0260612

水熱法による備Yang化Ge及びその常温低濃度一酸化窒素触媒性能【JST・京大機械翻訳】

Hydrothermal Fabrication and Catalytic Performance of Chromium Oxide for Low-concentration NO Oxidation at Ambient Temperature

著者 (8件)： Wu Meijian (School of Materials Science and Engineering, Shanghai Jiao Tong University) ,  Gao Zhenyuan (National Engineering Research Center for Nanotechnology) ,  Yuan Jing (National Engineering Research Center for Nanotechnology) ,  Zhao Kunfeng (National Engineering Research Center for Nanotechnology) ,  Cai Ting (National Engineering Research Center for Nanotechnology) ,  Yang Ling (National Engineering Research Center for Nanotechnology) ,  Zhang Tao (National Engineering Research Center for Nanotechnology) ,  He Dannong (School of Materials Science and Engineering, Shanghai Jiao Tong University, National Engineering Research Center for Nanotechnology)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 11  ページ： 1191-1197  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 酸化クロム触媒を,鋳型としてセチルトリメチルアンモニウムブロミド(CTAB),沈殿剤としてアンモニアを用いて,水熱法によって合成した。X線回折(XRD),FOURIER変換赤外分光法(FT-IR),X線光電子分光法(XPS),および透過型電子顕微鏡(TEM)を用いて,触媒の物理化学的性質を特性評価した。NOの初期酸化に対するNOの初期濃度の影響を研究した。結果は以下を示す。100°Cの水熱温度で調製したCR-100触媒は,1/10の空間速度で,1×10(-6)のNO濃度で,90%以上のNO除去率を示し,そして,NO除去率は,90%以上であった。その優れた室温触媒性能は触媒表面のCR(6+)/CR(3+)モル比に依存した。研究結果は以下を示す。触媒の不活性化は主に硝酸基が触媒表面の蓄積により触媒活性中心が被覆され,低濃度では根の蓄積が遅くなった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *触媒 ,  空間速度 ,  *触媒活性 ,  硝酸 ,  キャラクタリゼーション ,  沈殿試薬 ,  X線光電子分光法 ,  アンモニア ,  *水熱合成 ,  透過型電子顕微鏡 ,  酸化クロム ,  *一酸化窒素 ,  不活性化
準シソーラス用語： 除去率 ,  *低濃度 , 【Automatic Indexing@JST】

著者キーワード (4件)： hydrothermal ,  ambient temperature ,  deactivation ,  chromic oxide

分類 (5件)： 光化学一般  (CB08010U) ,  塩基,金属酸化物  (CD01030Z) ,  静電機器  (NB10020R) ,  炭素とその化合物  (YB02060D) ,  光化学反応  (CB08020F)

タイトルに関連する用語 (6件)： 水熱法 ,  Ge ,  常温 ,  低濃度 ,  一酸化窒素 ,  触媒性能