異なるMg/SiとCu含有量を持つPEG6000系合金の粒界腐食挙動【Powered by NICT】

The intergranular corrosion behavior of 6000-series alloys with different Mg/Si and Cu content

著者 (6件)： Zou Yun (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Liu Qing (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Jia Zhihong (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Xing Yuan (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Ding Lipeng (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China) ,  Wang Xueli (College of Materials Science and Engineering, Chongqing University, Chongqing, 400044, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 405  ページ： 489-496  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高CuまたはSiを過剰に添加した6000系アルミニウム合金は粒界腐食(IGC)に感受性であった。良好なIGC抵抗性を得るために,低/高Cuと種々のMg/Si比を有する四つの合金を設計した。四合金の腐食挙動を,加速腐食試験,電気化学的試験と電子顕微鏡で調べた。合金のIGC感受性は結晶粒界析出物の間のマイクロガルバニック結合と隣接した析出物フリーゾーン(PFZ)の結果,Cu含有量とMg/Si比の組み合わせに密接に関係することが明らかになった。過剰Mgは粒界に不連続析出物を形成することによって合金のIGC抵抗性を改善することができた。高Cuと過剰のMgを含む設計した合金は,低いCuと過剰Si市販合金,新しい合金を開発するための可能性を提供すると同じ腐食レベルを有していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *銅 ,  *マグネシウム ,  粒界析出 ,  *ケイ素 ,  *腐食 ,  *結晶粒界 ,  析出物 ,  アルミニウム合金 ,  電気化学 ,  不連続析出 ,  *粒界腐食 ,  *合金
準シソーラス用語： *腐食挙動 ,  *Cu含有量 , 【Automatic Indexing@JST】

著者キーワード (4件)： アルミニウム合金 ,  粒界腐食 ,  析出物 ,  電子顕微鏡観察

分類 (2件)： 金属薄膜  (BK14030T) ,  固体中の拡散一般  (BL06021L)

タイトルに関連する用語 (7件)： Mg ,  Si ,  Cu含有量 ,  PEG6000 ,  合金 ,  粒界 ,  腐食挙動