CO還元焼結プロセスにおける炭素挙動【JST・京大機械翻訳】

Carbon deposition behavior of reduction of sinter by carbon monoxide

著者 (5件)： Zhang Donghai (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology) ,  Wang Wei (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology) ,  Li Xiangwei (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology) ,  Zhu Hangyu (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology) ,  Xue Zhengliang (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology)
資料名： Gangtie Yanjiu Xuebao  (Gangtie Yanjiu Xuebao)
巻： 28  号： 8  ページ： 8-12  発行年： 2016年 
JST資料番号： W0829A  ISSN： 1001-0963  CODEN： GAYXEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 高炉中のCO還元焼結プロセスにおいて,炭素反応が起こり,高炉操業に悪影響を及ぼす。CS-8800型高周波赤外分光分析器を用いて,CO還元焼結プロセスにおける炭素挙動を分析し,NOVA400400型電界放出走査型電子顕微鏡を用いて,焼結後の焼結鉱の微細構造を分析した。研究結果は以下を示す。温度の上昇とともに,COの平衡濃度が高くなるほど,反応は起こりにくくなる。低温で析出した炭素は比較的多く、析出した炭素は主に焼結体の表面と気孔中に分布し、温度が比較的高い時には、炭素析出物のみが析出した。CO_2は,炭素反応に対して明らかな抑制効果を示した。析Tan量は還元時間の増加とともに増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 高炉操業 ,  走査電子顕微鏡 ,  *焼結 ,  低温 ,  HF【周波数】 ,  焼結鉱 ,  *炭素 ,  焼結体 ,  赤外分光分析 ,  高炉 ,  気孔 ,  電界放出
準シソーラス用語： 抑制効果 ,  炭素析出 ,  平衡濃度 , 【Automatic Indexing@JST】

著者キーワード (4件)： carbon deposition ,  sinter ,  reduction ,  microstructure