TaCセラミックスの微細構造と機械的性質に及ぼす焼結助剤としてV20mo1%ZrCと5mo1%Cu添加の影響【Powered by NICT】

Effects of adding 5-20mol% ZrC plus 5mol% Cu as a sintering aid on microstructure and mechanical properties of the TaC ceramics

著者 (5件)： Liu Limeng (School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan, 750021 China) ,  Geng Guihong (School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan, 750021 China) ,  Hai Wanxiu (School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan, 750021 China) ,  Chen Yuhong (School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan, 750021 China) ,  Wu Laner (School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan, 750021 China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 14  ページ： 16248-16254  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： TaCセラミックは,30MPaの機械的圧力下で30分間1900°Cでホットプレスにより調製した。圧密材料の緻密化,相組成,微細構造及び機械的性質に及ぼす焼結助剤として20mo1%ZrCまたは20mo1%ZrC+5mo1%Cuの添加の影響を調べた。結果は純粋なTaCは理論値の86%の相対密度を持つことを示した。密度>97%理論は,焼結助剤を用いた場合,材料で達成された。ZrC及びTaCが反応して固溶体を形成した。結晶粒平均サイズは20mo1%添加で純粋なTaCにおける18μmから6μmであった。5mo1%Cuの添加はさらにミクロ組織を微細化した。20mo1%ZrC mo1%Cuと10mo1%ZrC mo1%Cu組成は608MPaの良好な曲げ強さと破壊靭性5.4MPa√m~1/2であった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *微細構造 ,  精密化 ,  圧密 ,  相対密度 ,  *機械的性質 ,  曲げ強さ ,  緻密化 ,  固溶体 ,  破壊靱性 ,  相組成 ,  *セラミック ,  結晶粒 ,  ホットプレス
準シソーラス用語： *焼結助剤 , 【Automatic Indexing@JST】

著者キーワード (4件)： 超高温セラミック ,  炭化タンタル ,  Microstructure ,  機械的性質

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： TAC ,  セラミックス ,  微細構造 ,  機械的性質 ,  焼結助剤