NACL溶液中の異なる組織のA710鋼の耐食性を比較研究した。【JST・京大機械翻訳】

Corrosion Performance of Different Zones forWeld Joint of A710 Steel in 3.5%NaCl Solution

著者 (6件)： Hu Qian (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Liu Jing (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Wang Yukun (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Huang Feng (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Dai Mingjie (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Hou Yanglai (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology)
資料名： Zhongguo Fushi yu Fanghu Xuebao  (Zhongguo Fushi yu Fanghu Xuebao)
巻： 36  号： 6  ページ： 611-616  発行年： 2016年 
JST資料番号： W0862A  ISSN： 1005-4537  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 電気化学的試験と腐食減量法を用いて、3.5%NACL溶液中の異なる組織のA710鋼の耐食性を研究した。結果は以下を示す。3つの領域(母材(BM),熱影響部(HAZ),および溶接部(WM))のミクロ組織には,著しい差異があり,そして,フェライトは,主にフェライトおよびベイナイトから成り,そしてしかし、WMは主にベイナイト組織と少量の針状フェライトである。3.5%NACL溶液中のWMの電気化学的活性は最も高く,平均腐食速度は最大であった。16日間浸漬した後、腐食生成物は骨粗鬆症、保護性が悪く、母材上に多くの深い腐食が発生した。BMとHAZの腐食生成物は比較的緻密で、保護性が良く、母材の腐食は比較的に軽かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： フェライト ,  浸漬 ,  電気化学 ,  ベイナイト ,  腐食生成物 ,  *鋼 ,  骨粗鬆症 ,  溶接部 ,  腐食速度 ,  *耐食性
準シソーラス用語： アシキュラーフェライト ,  腐食減量 , 【Automatic Indexing@JST】

著者キーワード (4件)： A710 steel ,  microstructure ,  ocean engineering ,  corrosion product

分類 (2件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： NaCl ,  溶液 ,  組織 ,  耐食性 ,  研究