溶融ガスの溶接強度と靭性に及ぼす環境圧力の影響【JST・京大機械翻訳】

Influence of Environmental Pressure on Strength and Toughness of Weld by Gas Metal Arc Welding

著者 (6件)： Liu Hong (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology) ,  Xue Long (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology) ,  Huang Jiqiang (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology) ,  Huang Junfen (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology) ,  Feng Jing (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology) ,  Tan Yicheng (Opto-Mechatronic Equipment Technology Beijing Area Major Laboratory, Beijing Institute of Petro-Chemical Technology)
資料名： Shanghai Jiaotong Daxue Xuebao  (Shanghai Jiaotong Daxue Xuebao)
巻： 50  号： 10  ページ： 1613-1617  発行年： 2016年 
JST資料番号： W1060A  ISSN： 1006-2467  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 0.1MPA,0.5MPA,0.9MPAの圧力下で,高電圧溶接を用いて,Q235C鋼板を母材として用いて,溶接試験を行い,溶接電流,電圧,溶接速度,および溶接トーチの溶接パラメータを調整した。異なる環境圧力下で良好な溶接線を得て,溶接金属の機械的性質と微細構造を観察した。結果は以下を示す。環境圧力の増加とともに,溶接部の引張強さは増加し,靭性は明らかに低下し,溶接部およびその熱影響部のミクロ組織は,環境冷却効果の強化により,上部ベイナイト組織を形成したが,溶接継手の総合性能は,水中溶接関連規格の要求に適合した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 溶接電流 ,  電圧 ,  ベイナイト ,  溶接線 ,  *溶接 ,  溶接部 ,  溶接速度 ,  溶接継手 ,  溶接金属 ,  引張強さ ,  溶接トーチ ,  *靱性 ,  水中溶接
準シソーラス用語： 溶接パラメータ ,  *溶接強度 , 【Automatic Indexing@JST】

著者キーワード (4件)： underwater welding ,  gas metal arc welding (GMAW) ,  mechanical properties ,  microstructure

分類 (2件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 溶融 ,  溶接強度 ,  靭性 ,  環境圧力