文献

J-GLOBAL ID：201702238024584115   整理番号：17A0067335

高性能T型ゼオライト膜の調製とキャラクタリゼーションを行った。【JST・京大機械翻訳】

Preparation and Characterization of High Performance Zeolite T Membranes from Clear Solutions

著者 (6件)： Lv Youjia (School of Petroleum and Chemical Engineering, State Key Laboratory of Fine Chemicals, Dalian University of Technology, Panjin Campus) ,  Li Huazheng (School of Petroleum and Chemical Engineering, State Key Laboratory of Fine Chemicals, Dalian University of Technology, Panjin Campus) ,  Yang Jianhua (Institute of Adsorption and Inorganic Membrane, Dalian University of Technology) ,  Wang Jinqu (School of Petroleum and Chemical Engineering, State Key Laboratory of Fine Chemicals, Dalian University of Technology, Panjin Campus) ,  Yin Dehong (Institute of Adsorption and Inorganic Membrane, Dalian University of Technology) ,  Lu Jinming (Institute of Adsorption and Inorganic Membrane, Dalian University of Technology)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 7  ページ： 705-710  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 二次成長法を用いて,低密度のΑ-AL_2O_3管状担体上に連続的に緻密なシード層を調製し,モル比が1SIO_2であることを示した。0.05AL_2O_3;0.26NA_2O;0.09K_2O;T型ゼオライト膜を,120°C,16時間,30時間,30°Cで調製した。Tゼオライトゼオライト膜のモルフォロジーと特性に及ぼすマウスの濃度と結晶化時間の影響を研究した。XRDとSEMの結果は,結晶化過程における種晶のエピタキシャル成長と新しい核形成過程が同時に進行し,種晶のエピタキシャル成長と新核の誘導作用が相乗作用し,T膜の成長時間を短縮することを示した。調製したTゼオライトゼオライト膜を75°Cのパーベーパレーションで10WT%の水/イソプロパノール系に分離し,その透過流束と分離係数はそれぞれ2.96KG/(M2H)と6400であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 結晶化 ,  *キャラクタリゼーション ,  相乗作用 ,  X線回折 ,  パーベーパレーション ,  モル比 ,  種結晶 ,  透過流束 ,  モルフォロジー ,  分離係数
準シソーラス用語： 形成過程 ,  シード層 ,  低密度 ,  二次成長 ,  *ゼオライト膜 , 【Automatic Indexing@JST】

著者キーワード (4件)： T-type zeolite membrance ,  varying temperature hot dip-coating method ,  secondary growth ,  pervaporation

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (5件)： 高性能 ,  T型 ,  ゼオライト膜 ,  調製 ,  キャラクタリゼーション