Diels-Alder構造に基づくUV橋かけ可能なポリウレタンの合成,硬化プロセスと熱可逆的機構【Powered by NICT】

Synthesis, curing process and thermal reversible mechanism of UV curable polyurethane based on Diels-Alder structure

著者 (5件)： Ke Xiaoxue (College of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, PR China) ,  Liang Hongbo (College of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, PR China) ,  Xiong Lei (College of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, PR China) ,  Huang Shengmei (College of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, PR China) ,  Zhu Min (College of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, PR China)
資料名： Progress in Organic Coatings  (Progress in Organic Coatings)
巻： 100  ページ： 63-69  発行年： 2016年 
JST資料番号： A0541C  ISSN： 0300-9440  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： アクリレート機能とDiels-Alder(DA)構造を含む新規ポリウレタン樹脂を合成し,潜在的熱可逆性とUV硬化特性であった。UV硬化過程を,Fourier変換赤外分光法(FTIR)であり,これはDA構造は硬化プロセス過程で安定であり,最終アクリル酸CC転化率は82.5%であることを示したによりモニターした。硬化膜は良好な繰り返し熱可逆性を示した。硬化フィルムの逆Diels-Alder(rDA)反応は85.5°Cより高い温度で起こり,明らかに温度上昇,FTIR,示差走査熱量測定(DSC)及び動的熱機械分析(DMA)の結果によって確認されたにより促進された。硬化フィルムを熱重量分析(TGA)の結果によれば278.3°Cまで許容できる熱安定性をdisplaid。最後に,優れた物性を有する硬化膜が得られた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱安定性 ,  *ポリウレタン ,  昇温 ,  示差走査熱量測定 ,  熱重量分析 ,  転化率 ,  可逆性
準シソーラス用語： アクリラート ,  *紫外線硬化 , 【Automatic Indexing@JST】

著者キーワード (4件)： 熱可逆 ,  ポリウレタン ,  UV硬化 ,  Diels-Alder