MG-14ZN-5AL合金の部分的再溶融挙動に及ぼす初期微細構造の影響を研究した。【JST・京大機械翻訳】

Influence of original microstructure of Mg-14Zn-5Al alloy on partial remelting behavior

著者 (6件)： Li Chun (Department of Chemical Engineering and Modern Materials,Shangluo University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources) ,  Fan Xinhui (Department of Chemical Engineering and Modern Materials,Shangluo University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources) ,  Zhang Wenwen (Department of Chemical Engineering and Modern Materials,Shangluo University) ,  Han Xi (Department of Chemical Engineering and Modern Materials,Shangluo University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources) ,  Yang Chaopu (Department of Chemical Engineering and Modern Materials,Shangluo University, Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources) ,  Li Yuandong (State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals,Lanzhou University of Technology)
資料名： Bingqi Cailiao Kexue yu Gongcheng  (Bingqi Cailiao Kexue yu Gongcheng)
巻： 39  号： 5  ページ： 20-24  発行年： 2016年 
JST資料番号： C2398A  ISSN： 1004-244X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なる冷却速度でのMG-14ZN-5AL合金の鋳放し微細構造に及ぼす冷却速度の影響を研究した。結果は以下を示す。冷却速度の低下とともに,MG-10ZN-5AL合金の鋳放し微細構造は,微細な樹枝状→粗大樹枝状→等軸結晶粒を経験した。枝晶向の等軸結晶転移の初期組織が部分的に再溶解した後、その平均結晶粒度は先に増大し、その後増大する変化傾向を示し、その真円度は先に減少し、その後増大する変化傾向を示し、固相率の変化は大きくない。微細構造が微細な等軸結晶粒を主とするとき,MG-14ZN-5AL合金の平均結晶サイズは44.5~48.6ΜMであり,真円度は1.32~1.43であり,固相率は約60%であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 鋳放し ,  結晶粒度 ,  結晶粒 ,  真円度 ,  *微細構造 ,  結晶 ,  冷却速度 ,  溶解 ,  *合金
準シソーラス用語： 固相率 , 【Automatic Indexing@JST】

著者キーワード (4件)： original microstructure ,  remelting behavior ,  Mg-14Zn-5Al alloy ,  cooling rate