老化と海Shiの下での近海橋かけゴム材料の性能劣化試験【JST・京大機械翻訳】

Experimental research on property deterioration of rubber material used as natural rubber isolator for offshore bridges under aging and marine corrosion

著者 (5件)： Ma Yuhong (Guangdong Key Laboratory of Earthquake Engineering & Applied Technique, Earthquake Engineering Research & Test Center, Guangzhou University) ,  Zhao Guifeng (School of Civil Engineering, Guangzhou University) ,  Luo Jiarun (Guangdong Key Laboratory of Earthquake Engineering & Applied Technique, Earthquake Engineering Research & Test Center, Guangzhou University) ,  Cui Jie (Guangdong Key Laboratory of Earthquake Engineering & Applied Technique, Earthquake Engineering Research & Test Center, Guangzhou University) ,  Zhou Fulin (Guangdong Key Laboratory of Earthquake Engineering & Applied Technique, Earthquake Engineering Research & Test Center, Guangzhou University)
資料名： Zhendong yu Chongji  (Zhendong yu Chongji)
巻： 35  号： 16  ページ： 114-122,129  発行年： 2016年 
JST資料番号： C2157A  ISSN： 1000-3835  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ゴムとゴムブロックとの同じ材料からなるゴムブロックを設計し,ゴムブロックとゴムブロックとゴムブロックを同じ試験環境下で試験した。ゴム材料の硬度,弾性率,引張強さ,および破断伸度が,老化時間と厚さ方向に及ぼす影響を研究した。実験結果は以下を示す。老化はゴム材料の性質に影響する主な要因である。ゴムの含水量の高さはその性能に大きく影響する。老化時間の増加とともに,ゴムの硬度および弾性率は増加し,一方,引張強さおよび破断伸びは減少した。ゴムの硬度と弾性率に及ぼす純粋な海Shiの影響は明らかではないが,引張強さと破断伸びは海Shi時間の増加と共に減少する。老化++試験の結果は,老化効果と海Shi効果の重ね合わせであり,その結果,ゴムの性能劣化は,より大きい歪の下でより明白であった。ゴムの表面から内部まで,ゴム材料の性能はわずかに減少する傾向を示し,老化と海Shiは基本的に表面に発生したが,内部ゴムの性能はわずかに変化した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *近海 ,  引張強さ ,  重合せ ,  硬度 ,  含水量 ,  *海洋 ,  弾性係数
準シソーラス用語： 破断伸び ,  破断伸度 ,  *性能劣化 , 【Automatic Indexing@JST】

著者キーワード (5件)： offshore bridge ,  aging ,  marine corrosion ,  natural rubber ,  property deterioration

分類 (4件)： ゴム  (YH07020M) ,  機械的性質  (YH02022L) ,  構造力学一般  (HD01000X) ,  充填剤,補強材  (YH05030J)

タイトルに関連する用語 (7件)： 老化 ,  海 ,  近海 ,  橋かけ ,  ゴム材料 ,  性能劣化 ,  試験