Liイオン電池熱管理のための複合相変化物質/膨張黒鉛の熱的最適化【Powered by NICT】

Thermal optimization of composite phase change material/expanded graphite for Li-ion battery thermal management

著者 (5件)： Jiang Guiwen (Department of Materials Forming & Controlling Engineering, Nanchang University, Nanchang 330031, China) ,  Huang Juhua (Department of Materials Forming & Controlling Engineering, Nanchang University, Nanchang 330031, China) ,  Fu Yanshu (Department of Materials Forming & Controlling Engineering, Nanchang University, Nanchang 330031, China) ,  Cao Ming (Department of Materials Forming & Controlling Engineering, Nanchang University, Nanchang 330031, China) ,  Liu Mingchun (Department of Materials Forming & Controlling Engineering, Nanchang University, Nanchang 330031, China)
資料名： Applied Thermal Engineering  (Applied Thermal Engineering)
巻： 108  ページ： 1119-1125  発行年： 2016年 
JST資料番号： E0667B  ISSN： 1359-4311  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 増強された熱伝導率を持つパラフィン(RT44HC)/膨張黒鉛(EG)複合相変化材料(CPCM)は,Liイオン電池の熱管理を改善した。これらの電池の熱管理は,CPCM組成を最適化することによりさらに改良されるであろう。本研究では,EGの種々の質量分率を持つ,CPCMの熱管理性能は,Liイオン電池に対して調べた。多孔質EGにRT44HCを吸収することによって調製したCPCM試料。,熱伝導率および液相変化材料(PCM)漏出のような複合材料の特性を測定した。著者らの結果は以下のことを示した:(1)EG導入はCPCMの熱伝導率を劇的に促進し,Liイオン電池の温度上昇の有意な減少をもたらすおよび(2),EG質量分率9%から20%に変化させた,CPCMは優れた熱管理性能を示した。EG負荷量の増加と共に減少する,液体PCM漏出は相転移中に起こった。,相転移中の液体PCM漏れを考慮に入れて,16 20wt%EG CPCMはLiイオン電池の熱管理のための最も有望な代替と見なすことができることを提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： パラフィンワックス ,  *イオン ,  昇温 ,  *電池 ,  *最適化 ,  多孔性 ,  *熱管理 ,  相転移 ,  熱伝導率 ,  *リチウム ,  複合材料
準シソーラス用語： 負荷量 ,  質量分率 ,  *膨張黒鉛 ,  *相変化材料 , 【Automatic Indexing@JST】

著者キーワード (5件)： 相変化材料 ,  膨張黒鉛 ,  熱伝導率 ,  熱管理 ,  Liイオン電池