マグネトロンスパッタリングにより調製したCEO_2/PTFE/NAFION複合膜の特性を研究した。【JST・京大機械翻訳】

Properties of CeO_2 /PTFE/Nafion Composite Membranes Prepared by Magnetron Sputtering

著者 (7件)： Xia Qingcheng (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Mao Fei (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Yang Yong (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Han Jing (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Liu Xiaohui (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Yang Jiazhi (School of Chemical Engineering,Nanjing University of Science and Technology) ,  Sun Dongping (School of Chemical Engineering,Nanjing University of Science and Technology)
資料名： Gaodeng Xuexiao Huaxue Xuebao  (Gaodeng Xuexiao Huaxue Xuebao)
巻： 37  号： 11  ページ： 2108-2116  発行年： 2016年 
JST資料番号： C2116A  ISSN： 0251-0790  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： CEO_2/PTFE複合膜を,ポリテトラフルオロエチレン(PTFE)膜上にマグネトロンスパッタリングにより調製した。接触角,X線光電子分光法(XPS),走査電子顕微鏡(SEM)および引張強さを用いて,複合膜の親水性,元素組成,形態および機械的強度を測定し,スパッタリング時間およびスパッタリングパワーが膜性能に及ぼす影響を研究した。結果は,40Wのスパッタリングパワーと120Sのスパッタリング時間で,CEO_2/PTFE複合材料の水性と引張強さが比較的良いことを示した。CEO_2/PTFE複合膜上にNAFION樹脂をキャストすることにより,CEO_2/PTFE/NAFION複合膜の含水量は30%に達し,イオン伝導率は0.071S/CMに達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 複合材料 ,  X線光電子分光法 ,  *マグネトロンスパッタリング ,  *ポリテトラフルオロエチレン ,  走査電子顕微鏡 ,  機械的強度 ,  *複合膜 ,  含水量 ,  引張強さ ,  *スパッタリング ,  接触角 ,  親水性
準シソーラス用語： イオン伝導率 ,  元素組成 , 【Automatic Indexing@JST】

著者キーワード (4件)： Polytetrafluoroethylene (PTFE) microporous membrane ,  Magnetron sputtering ,  Contact angle ,  Tensile strength

分類 (3件)： その他の無機化合物の薄膜  (BK14060A) ,  その他の無機化合物の結晶構造  (BK07030J) ,  膜分離  (XD02120Z)

タイトルに関連する用語 (6件)： マグネトロンスパッタリング ,  調製 ,  PTFE ,  Nafion ,  複合膜 ,  研究