Temperature dependence of twinning and magnetic stresses in Ni₄₆Mn₂₄Ga₂₂Co₄Cu₄ alloy with giant 12% magnetic field-induced strain

著者 (6件)： Sozinov A. (Lappeenranta University of Technology, Material Physics Laboratory, Laitaatsillantie 3, FI-57170 Savonlinna, Finland) ,  Soroka A. (Lappeenranta University of Technology, Material Physics Laboratory, Laitaatsillantie 3, FI-57170 Savonlinna, Finland) ,  Lanska N. (Lappeenranta University of Technology, Material Physics Laboratory, Laitaatsillantie 3, FI-57170 Savonlinna, Finland) ,  Rames M. (Institute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 1999/2, CZ-182 21 Prague, Czech Republic) ,  Straka L. (Institute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 1999/2, CZ-182 21 Prague, Czech Republic) ,  Ullakko K. (Lappeenranta University of Technology, Material Physics Laboratory, Laitaatsillantie 3, FI-57170 Savonlinna, Finland)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 131  ページ： 33-36  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： は12%までの磁場誘起歪(MFIS)を示す磁気形状記憶合金Ni_46Mn_24Ga_22Co_4Cu_4を研究した。MFISが変調されてない正方結晶格子中の化合物双晶境界(CTB)の運動により仲介される。双晶応力σ(T),正方晶性比,および磁気異方性エネルギー密度K(T)の温度依存性,磁気応力σ(T)計算を示した。温度の上昇と共に,CTBの双晶応力は 0.02MPa/Kの勾配で減少し,2回10M Ni-Mn-GaマルテンサイトにおけるI型双晶境界で観察されたよりも遅かった。温度窓の存在,その中で巨大MFISが観察されるを発見し,説明した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *温度依存性 ,  正方晶系 ,  *合金 ,  性比 ,  *双晶 ,  磁気異方性 ,  結晶格子 ,  *磁気 ,  形状記憶効果 ,  双晶境界 ,  マルテンサイト
準シソーラス用語： Ni-Mn-Ga ,  異方性エネルギー ,  磁気形状記憶合金 ,  *磁場誘起 , 【Automatic Indexing@JST】

著者キーワード (5件)： ホイスラー相 ,  強磁性形状記憶合金 ,  双晶化 ,  磁気異方性 ,  磁気形状記憶

分類 (3件)： 変態組織,加工組織  (WB01030N) ,  その他の金属組織学  (WB01040Y) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 磁場誘起 ,  ひずみ ,  双晶 ,  温度依存性