活性炭とそのヒドラジン分解への熱炭素アンモニア還元によるナノ構造タングステン炭窒化物(WN-x C_y)の合成【Powered by NICT】

Synthesis of nanostructured tungsten carbonitride (WN _x C _y ) by carbothermal ammonia reduction on activated carbon and its application in hydrazine decomposition

著者 (4件)： Sun Jun (State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, 457 Zhongshan Road, Dalian 116023, China) ,  Liang Binglian (State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, 457 Zhongshan Road, Dalian 116023, China) ,  Huang Yanqiang (State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, 457 Zhongshan Road, Dalian 116023, China) ,  Wang Xiaodong (State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, 457 Zhongshan Road, Dalian 116023, China)
資料名： Catalysis Today  (Catalysis Today)
巻： 274  ページ： 123-128  発行年： 2016年10月01日 
JST資料番号： T0363A  ISSN： 0920-5861  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 炭素源と窒素源として支援炭素とNH_3を用いたナノ構造タングステン炭窒化物の合成のために導入した炭素熱NH_3低減法。WO_3/ACからこの経路によって合成した一連の試料を,X線回折,昇温表面反応質量分光法,透過型電子顕微鏡,及び微小熱量測定によって特性化した。結果はナノ構造タングステン炭窒化物(WN_ _y)は800°Cで活性化した炭素上に合成することに成功し,得られたWN_ _yは2nm未満の粒径を有する炭素担体上に均一に分散したことを示した。炭素熱NH_3プロセスによって調製されたWN_ _y/ACはCO吸着の強い能力を持ち,炭素熱H_2還元法で作製したWC_x/AC H触媒よりもヒドラジン分解のための良好な触媒性能を示した。さらにベンチスケール試験は,ヒドラジン分解技術の伝統的Ir/Al_2O_3触媒の有望な代替であることを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *タングステン ,  *ヒドラジノリシス ,  粒径 ,  X線回折 ,  *炭素 ,  触媒活性 ,  透過型電子顕微鏡 ,  昇温 ,  *アンモニア ,  熱量測定 ,  *活性炭 ,  表面反応 ,  *ナノ構造 ,  キャラクタリゼーション
準シソーラス用語： *炭窒化物 , 【Automatic Indexing@JST】

著者キーワード (5件)： ヒドラジン分解 ,  活性炭 ,  炭窒化タングステン ,  Microcalorimetry ,  マイクロスラスタ

分類 (1件)： その他の触媒  (CB06123Z)

タイトルに関連する用語 (8件)： 活性炭 ,  ヒドラジン分解 ,  炭素 ,  アンモニア ,  還元 ,  ナノ構造 ,  タングステン ,  炭窒化物