カーバイドスラグの結晶化速度論を,種々の雰囲気下で研究した。【JST・京大機械翻訳】

Crystallization Kinetics of Carbide Slag under Different Atmospheres

著者 (7件)： Liu Hongpan (Faculty of Environmental Science and Engineering,Kunming University of Science and Technology) ,  Huang Xiaofeng (Faculty of Environmental Science and Engineering,Kunming University of Science and Technology) ,  Jiang Ming (College of Resources and Environment,Yunnan Agricultural University) ,  Ma Liping (Faculty of Environmental Science and Engineering,Kunming University of Science and Technology) ,  Shang Zhibiao (Faculty of Environmental Science and Engineering,Kunming University of Science and Technology) ,  Bai Pingzhen (College of Resources and Environment,Yunnan Agricultural University) ,  Tang Baiping (No. 2 Middle School,Lingchuan Country)
資料名： Guisuanyan Tongbao  (Guisuanyan Tongbao)
巻： 35  号： 11  ページ： 3715-3719,3728  発行年： 2016年 
JST資料番号： C2439A  ISSN： 1001-1625  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： カーバイドスラグを研究対象として、熱分析により、異なる雰囲気下の炭化物の熱分解過程を研究し、カーバイドスラグの分解による生成物を溶融法により、CAO-AL_2O_3-SIO_2系ガラスセラミックを調製した。示差熱分析により、修正したJOHNSON-MEHL-AVRAMI(JMA)方程式とAUGIS-BENNETT方程式を利用して、異なる雰囲気下でのカーバイドスラグの微結晶ガラス過程における結晶化規則を分析した。結果は以下を示す。異なる雰囲気の下で,カーバイドスラグの重量損失率は異なり,窒素雰囲気下で,カーバイドスラグの重量損失率は22.66%であった。一方,空気中での炭化物の重量損失は%%であった。結晶化挙動を研究し,窒素雰囲気中での結晶化の活性化エネルギーは310.99KJ/MOLであり,結晶化の活性化エネルギーは353.43KJ/MOL以下であった。AUGIS-BENNETT方程式により,異なる雰囲気での結晶化機構を研究し,窒素雰囲気下での其晶化機構は三次元体積結晶化により進行し,空気雰囲気では二維晶化方式で進行することがわかった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： ガラスセラミック ,  *結晶化 ,  熱分析 ,  活性化エネルギー ,  示差熱分析 ,  重量損失 ,  炭化物 ,  三次元 ,  微結晶 ,  熱分解 ,  ガラス ,  *晶析速度 ,  窒素雰囲気
準シソーラス用語： 結晶化挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： carbide slag ,  nitrogen atmosphere ,  air atmosphere ,  thermal decomposition ,  crystallization kinetics

分類 (3件)： 非晶質金属の構造  (BK04020D) ,  その他の無触媒反応  (CB06070U) ,  有機化合物の化学分析  (CC07034C)

タイトルに関連する用語 (3件)： 結晶化速度論 ,  雰囲気 ,  研究