産An菌の化学的変異誘発と浸出低品位銅鉱試験の研究【JST・京大機械翻訳】

Experimental study on chemical mutation of ammonia-producing bacteria and bioleaching of low grade copper ore

著者 (4件)： Hu Kaijian (Key Laboratory of Ministry of Education for Efficient Mining and Safety of Metal Mines, University of Science and Technology Beijing) ,  Wu Aixiang (Key Laboratory of Ministry of Education for Efficient Mining and Safety of Metal Mines, University of Science and Technology Beijing) ,  Wang Hongjiang (Key Laboratory of Ministry of Education for Efficient Mining and Safety of Metal Mines, University of Science and Technology Beijing) ,  Wang Shaoyong (Key Laboratory of Ministry of Education for Efficient Mining and Safety of Metal Mines, University of Science and Technology Beijing)
資料名： Zhongnan Daxue Xuebao Zirankexueban  (Zhongnan Daxue Xuebao Zirankexueban)
巻： 47  号： 10  ページ： 3289-3294  発行年： 2016年 
JST資料番号： C2798A  ISSN： 1672-7207  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 性 JAT-1を,アルカリ性AMMONIAGENES 1-1として同定した。原始菌種として,ヒドロキシルアミン塩酸塩を用いて化学的変異誘発を行い,変異誘発前後の細菌活性,形態および浸出能力の変化を調べた。研究結果は以下を示す。塩酸ヒドロキシルアミンの変異誘発作用は細菌の活性を高め,銅の浸出能力を向上させる。1.5%(質量分率)のヒドロキシルアミン塩酸塩は最適誘導剤含量であり、この条件下で細菌の致死率は81.00%、正突然変異率は16.67%であった。誘変前の細菌と比較して,突然変異後の細菌成長は10時間安定し,安定した細菌濃度は%%増加し,産An量は17.60%増加し,突然変異後の細菌のサイズと形状は変化しなかったが,表面分泌物は増加した。突然変異菌による銅鉱石の浸出は168時間後の銅浸出率は58.52%に達し,それは誘変前のそれより%%高かった。浸出後、鉱石表面の細粒鉱物が消失し、鉱石表面に結晶や沈殿が形成されず、表面の結晶粒が明らかに増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *浸出 ,  分泌物 ,  結晶粒 ,  致死率 ,  *銅鉱 ,  細菌 ,  鉱石 ,  *銅 ,  *変異誘発 ,  突然変異
準シソーラス用語： 銅浸出 ,  変異率 ,  質量分率 ,  細菌活性 ,  アルカリ性 , 【Automatic Indexing@JST】

著者キーワード (5件)： low grade copper ore ,  bioleaching ,  chemical mutation ,  bacterial ,  ammonia