硫酸塩アタックに暴露した再生コンクリート微粉と骨材を用いた自己充填コンクリートの性能【Powered by NICT】

Performance of self-compacting concrete incorporating recycled concrete fines and aggregate exposed to sulphate attack

著者 (5件)： Boudali S. (Department of Civil Engineering, University of Sciences and Technology of Oran Mohamed Boudiaf, Oran, Algeria) ,  Kerdal D.E. (Department of Civil Engineering, Laboratory LM2SC-USTOMB, University of Sciences and Technology of Oran Mohamed Boudiaf, Oran, Algeria) ,  Ayed K. (Department of Civil Engineering, Laboratory LABMAT-ENPO, National Polytechnic of Oran, Oran, Algeria) ,  Abdulsalam B. (Department of Civil and Environment Engineering, Western University, London, Ontario, Canada) ,  Soliman A.M. (Department of Building, Civil and Environment Engineering, Concordia University, Montreal, Quebec, Canada)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 124  ページ： 705-713  発行年： 2016年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,種々の硫酸環境下における再生コンクリート微粉と骨材を組込んだ自己充填コンクリート(SCC)と自己充填コンクリート(SCSC)の性能を調べた。天然骨材と天然ポゾランを含む同様の混合物も比較のために試験した。異なる硫酸塩作用領域(すなわち完全浸漬および浸漬-乾燥サイクル)を適用した。硫酸塩攻撃下での圧縮強度発現/分解は全てのテスト混合物において監視した。結果はリサイクル材料の使用は,天然材料との混合物に関して強度発現に有意に影響しなかったことを示した。さらに,再生コンクリート骨材と再生コンクリート細)を使用した混合物は天然骨材と天然ポゾランを持つそれらよりも良好な硫酸抵抗挙動を示した。結論として,使用した再生材料の品質は,グリーンで持続可能な自己充填性コンクリートを製造する上で重要な因子である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 天然材料 ,  浸漬 ,  *硫酸塩 ,  *硫酸 ,  耐久性 ,  強度発現 ,  *再生コンクリート ,  リサイクル ,  *微粉体 ,  ポゾラン
準シソーラス用語： 持続可能 ,  再生材料 ,  コンクリート骨材 ,  天然骨材 ,  *自己充填コンクリート , 【Automatic Indexing@JST】

著者キーワード (5件)： 耐久性 ,  Strength ,  再生コンクリート ,  ポゾラン ,  硫酸塩攻撃

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (6件)： 硫酸塩 ,  暴露 ,  再生コンクリート ,  微粉 ,  骨材 ,  自己充填コンクリート