リチウムイオン電池のためのアノードとしての卵黄-シェル構造をもつSi-Cナノ複合材料の容易な合成【Powered by NICT】

Facile synthesis of Si-C nanocomposites with yolk-shell structure as an anode for lithium-ion batteries

著者 (6件)： Ma Yiheng (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072, China) ,  Tang Haoqing (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072, China) ,  Zhang Yao (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072, China) ,  Li Zhoufu (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072, China) ,  Zhang Xinhe (McNair Technology Company Limited, Dongguan City, Guangdong, 523700, China) ,  Tang Zhiyuan (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 704  ページ： 599-606  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 卵黄-殻構造化Siベースアノードは犠牲層とCVDプロセスとして,SiO_2の代わりにMgOを堆積することにより合成した。HFエッチングは希釈H Clを用いて置換することができ,これは毒性と腐食性であった。結果は卵黄-シェル構造を首尾よく合成し,改善された電気化学性能を持つことを示した。MgO被覆の量も調べた。MgOとSiの適切な質量比は約2で,901mAh/g~( 1)と88.3%保持の可逆的充電容量は1.0Ag~( 1)で100サイクル後に達成された。サイクル性能の著しい改善は,この研究で卵黄-殻構造化Si-Cナノ複合材料はリチウムイオン電池の有望なアノード材料であることを示す。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 電気化学 ,  構造形成 ,  希釈 ,  *卵黄 ,  *シェル構造 ,  *ケイ素 ,  酸化マグネシウム ,  *ナノ複合材料 ,  エッチング ,  *リチウムイオン電池
準シソーラス用語： 負極材料 ,  サイクル性能 ,  充電容量 ,  質量比 ,  犠牲層 , 【Automatic Indexing@JST】

著者キーワード (5件)： シリコン ,  ナノ複合材料 ,  卵黄殻構造 ,  アノード ,  リチウムイオン電池

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (6件)： リチウムイオン電池 ,  アノード ,  卵黄 ,  シェル構造 ,  Si ,  ナノ複合材料