ZNO/ZNOナノ複合材料はZNOベース熱電材料の性能を改良した。【JST・京大機械翻訳】

PPP Addition to Improve Thermoelectric Properties of ZnO-based Thermoelectric Composites

著者 (6件)： Wu Zihua (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University) ,  Xie Huaqing (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University) ,  Wang Yuanyuan (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University) ,  Mao Jianhui (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University) ,  Xing Jiaojiao (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University) ,  Li Yihuai (School of Environment and Materials Engineering, College of Engineering, Shanghai Polytechnic University)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 11  ページ： 1249-1254  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： PPP@ZN_(1-X)CO_XOナノ複合材料(X=0,0.025)をゾル-ゲル法により合成し,放電プラズマ焼結により調製し,その熱電特性を調べた。透過型電子顕微鏡写真から,PPPナノ粒子のサイズは200NM以下であることがわかった。熱電性能解析により,PPP添加量の増加とともに,熱伝導率は,最初に増加し,次に減少した。電気伝導率はPPP含有量の増加と共に大幅に向上した。ZNOバルク材料と比較して,ゾル-ゲル法によって合成したPPP@ZN_(1-X)CO_XOナノ複合材料の熱伝導率は,640Kで,5.4W/(MK)に低下した。電気伝導率の増加と熱伝導率の低下により、熱電性能が大幅に向上し、9WT%PPP@ZN_(0.975)CO_(0.025)Oナノ複合材料は870Kで最大ZT値(0.16)を持つ。それはZN_(0.975)CO_(0.025)O材料の8倍であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 透過型電子顕微鏡 ,  電気伝導率 ,  ゾル-ゲル法 ,  ナノ粒子 ,  放電プラズマ焼結 ,  性能分析 ,  *ナノ複合材料 ,  熱伝導率 ,  *熱電材料
準シソーラス用語： 熱電特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： ZnO ,  thermoelectric property ,  Sol-Gel ,  molecular junction

分類 (1件)： 熱電デバイス  (NC03090J)

タイトルに関連する用語 (3件)： ZnO ,  ナノ複合材料 ,  熱電材料