BA_(1-X)TIO_3ナノ結晶とその誘電性とマイクロ波吸収特性を室温での界面活性剤によって合成した。【JST・京大機械翻訳】

A surfactant-free route to synthesize Ba_xSr_(1-x)TiO_3 nanoparticles at room temperature, their dielectric and microwave absorption properties

著者 (5件)： Wu Qingsong (Division of Nanomaterials & Chemistry, Department of Chemistry, University of Science and Technology of China) ,  Liu Jianwei (Division of Nanomaterials & Chemistry, Department of Chemistry, University of Science and Technology of China) ,  Wang Guangsheng (Division of Nanomaterials & Chemistry, Department of Chemistry, University of Science and Technology of China) ,  Chen Shaofeng (Division of Nanomaterials & Chemistry, Department of Chemistry, University of Science and Technology of China) ,  Yu Shuhong (Division of Nanomaterials & Chemistry, Department of Chemistry, University of Science and Technology of China)
資料名： Zhongguo Kexue. Cailiao Kexue  (Zhongguo Kexue. Cailiao Kexue)
巻： 59  号： 8  ページ： 609-617  発行年： 2016年 
JST資料番号： C2863A  ISSN： 2095-8226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： それらの優れた強誘電性,強誘電性,誘電性,圧電性,および電気的性質のため,ペロブスカイト材料,特にチタン酸バリウムストロンチウム(BA_XSR_(1-X)TIO_3)が広く注目されている。本論文では,簡易(BA_XSR_(1-X)TIO_3)ナノ結晶を,表面,塩化ストロンチウム水溶液,およびイソプロパノールのエタノール水溶液の混合によって調製した。バリウム/ストロンチウムのモル比は,塩化バリウムと塩化ストロンチウムの初期供給比を変えることによって,正確に制御することができた。生成物の誘電特性とマイクロ波吸収特性を研究し,その結果,X=0.7の場合に,生成物の誘電特性とマイクロ波吸収特性が最適化されることを示した。この合成法は,温和な条件,低コスト,高収率で,他のペロブスカイト材料の調製のための新しい方法を提供した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *界面活性剤 ,  *ナノ結晶 ,  モル比 ,  強誘電性 ,  塩化ストロンチウム ,  *誘電性 ,  塩化バリウム ,  圧電気 ,  水溶液 ,  最適化 ,  電気的性質 ,  脂肪族アルコール
準シソーラス用語： チタン酸バリウムストロンチウム ,  *マイクロ波吸収 , 【Automatic Indexing@JST】

著者キーワード (5件)： perovskite ,  crystallization ,  dielectric ,  microwave absorption ,  mixed solution

分類 (1件)： 強誘電体,反強誘電体,強弾性  (BM05030B)

物質索引 (1件)： エタノール

タイトルに関連する用語 (5件)： ナノ結晶 ,  誘電性 ,  マイクロ波吸収 ,  室温 ,  界面活性剤