[111]-分極(Na, K)(Nb,Ta)O_3鉛フリー単結晶の完全なテンソル特性【Powered by NICT】

Full tensor properties of [111] poled (Na, K)(Nb,Ta)O₃ lead-free single crystal

著者 (6件)： Jing Yujia (Condensed Matter Science and Technology Institute, Harbin Institute of Technology, Harbin 150001, China) ,  Lu Xiaoyan (School of Civil Engineering, Harbin Institute of Technology, Harbin 150001, China) ,  Zheng Limei (Condensed Matter Science and Technology Institute, Harbin Institute of Technology, Harbin 150001, China) ,  Yang Liya (Condensed Matter Science and Technology Institute, Harbin Institute of Technology, Harbin 150001, China) ,  Zhang Rui (Condensed Matter Science and Technology Institute, Harbin Institute of Technology, Harbin 150001, China) ,  Li Yuanyuan (School of Chemistry and Chemical Engineering, Henan University of Technology, Zhengzhou 450001, China)
資料名： Materials Letters  (Materials Letters)
巻： 186  ページ： 267-270  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： [111]分極した(Na,K)(Nb, Ta)O_3単結晶の弾性,圧電および誘電定数の完全セットを測定した。結果は「三+零」分域構造をもつ結晶は高いせん断が低縦圧電特性(d15=140pC/N,15=0.569,d_33=64pC/NとK_33=0.450)であり,「一零」単分域状態に類似しているが,「四零」マルチドメイン状態とは異なって示すことが分かった。方位に依存する縦方向特性,例えば,(01 1)C面における33日,33*,33sと33*を計算した。最大圧電気は[011]から38°の位置で存在し,それは[111]方向に近かった。測定と計算したパラメータを比較することによって,圧電性は固有の寄与が優勢で,一方,誘電性は外因的寄与によって制御されると結論できる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 弾性 ,  *単結晶 ,  誘電性 ,  圧電気 ,  誘電率 ,  *テンソル ,  分域構造 ,  *分極
準シソーラス用語： 単分域 ,  圧電特性 ,  *鉛フリー , 【Automatic Indexing@JST】

著者キーワード (3件)： Ferroelectrics ,  圧電材料 ,  誘電体

分類 (3件)： 圧電気,焦電気,エレクトレット  (BM05040M) ,  セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (7件)： 分極 ,  Na ,  Nb ,  Ta ,  鉛フリー ,  単結晶 ,  テンソル