CR_XCU_1FE_2MO_(0.5)NB_(0.5)NI_2高合金のミクロ組織と機械的性質に及ぼす時効処理の影響を研究した。【JST・京大機械翻訳】

Effect of Aging Treatment on Microstructure and Mechanical Properties of CrxCuFe_2Mo_(0.5)Nb_(0.5)Ni_2High-entropy Alloys

著者 (8件)： Liu Niucan (School of Science,Henan Institute of Engineering) ,  Zhao Ruifeng (School of Science,Henan Institute of Engineering) ,  Ren Bo (School of Mechanical Engineering,Henan Institute of Engineering) ,  Zhang Hongsong (School of Mechanical Engineering,Henan Institute of Engineering) ,  Guan Shaokang (School of Materials Science and Engineering,Zhengzhou University) ,  Jiang Haijing (School of Mechanical Engineering,Henan Institute of Engineering) ,  Wang Xiaowei (School of Mechanical Engineering,Henan Institute of Engineering) ,  Shi Mengchuan (School of Mechanical Engineering,Henan Institute of Engineering)
資料名： Tezhong Zhuzao ji Youse Hejin  (Tezhong Zhuzao ji Youse Hejin)
巻： 36  号： 12  ページ： 1312-1315  発行年： 2016年 
JST資料番号： C2364A  ISSN： 1001-2249  CODEN： TZJHEE  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： CR_XCU_1FE_2MO_(0.5)NB_(0.5)NI_2(X=0,0.5,1.0,2.0,C1~C4合金)を,非消耗真空アーク融解によって調製700°Cと800°Cで12時間アニールした後に,微細構造と硬度を分析した。その結果,CR_XCUFE_2MO_(0.5)NB_(0.5)NI_2合金は,BCC相,FCC相およびHCP相から成り,700°Cでアニールした後に,合金の相は明らかに変化せ800°Cでアニールした後,C2合金の他の合金のFCC相はBCC相に変化した。CR_XCUFE_2MO_(0.5)NB_(0.5)NI_2合金のミクロ組織は,700°Cと800°Cで焼鈍した後に,樹枝状晶と樹枝状晶間のミクロ組織を示しCR_XCUFE_2MO_(0.5)NB_(0.5)NI_2合金の硬度は,鋳放し,700°Cおよび800°CでのCR含有量の増加とともに増加したが,増加幅は小さかった。800°Cで焼なましした後,C4合金の硬度(HV)は441から480に増加し,伸びは8.8%であり,比較的弱い時効硬化現象を示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 焼なまし ,  鋳放し ,  *合金 ,  微細構造 ,  伸び ,  機械的性質 ,  硬度 ,  時効硬化 ,  アーク融解 ,  樹枝状結晶

著者キーワード (4件)： High Entropy Alloy ,  Aging Treatment ,  Microstructure ,  Hardness

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 高合金 ,  ミクロ組織 ,  機械的性質 ,  時効処理 ,  研究