文献

J-GLOBAL ID：201702246649427139   整理番号：17A0471513

溶融アンモニウムふっ化水素中の陽極酸化による生物医学的マグネシウム合金の制御可能な分解を達成【Powered by NICT】

Achieving controllable degradation of a biomedical magnesium alloy by anodizing in molten ammonium bifluoride

著者 (4件)： Jiang Heng Bo (Department and Research Institute of Dental Biomaterials and Bioengineering, College of Dentistry, Yonsei University, Seoul 03722, Republic of Korea) ,  Wu Guosong (Plasma Bioscience Research Center, Kwangwoon University, Seoul 01897, Republic of Korea) ,  Lee Sang-Bae (Department and Research Institute of Dental Biomaterials and Bioengineering, College of Dentistry, Yonsei University, Seoul 03722, Republic of Korea) ,  Kim Kwang-Mahn (Department and Research Institute of Dental Biomaterials and Bioengineering, College of Dentistry, Yonsei University, Seoul 03722, Republic of Korea)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 313  ページ： 282-287  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： マグネシウム(Mg)および生分解性金属材料としてその合金は整形外科および心臓血管材料の分野における基礎研究されている。しかし,マグネシウムインプラントは貧弱な耐食性,特に生理的環境,医学的応用を制限するのを示した。Mgの耐食性を改善するために,陽極酸化はフッ化物電解質の超高濃度に適用した。,表面形態,皮膜の厚さと組成を決定し,陽極酸化Mg合金の腐食挙動を評価した。陽極酸化による被覆の結果は,細孔径600~900nmのと14μmの厚さの多孔性構造はMg合金基板上に発生し,この被覆成分はふっ化マグネシウムであることを示した。電気化学的腐食試験および浸漬腐食試験では,陽極酸化Mg合金を試験し,陽極酸化Mg合金は,シミュレートした体液(SBF)中の未処理Mg合金と比較して有意に改善された耐食性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *マグネシウム ,  微生物分解性 ,  電気化学的腐食試験 ,  *アノード酸化 ,  多孔性 ,  浸漬 ,  *マグネシウム合金 ,  *合金 ,  耐食性 ,  電解 ,  フッ化マグネシウム ,  *フッ化水素 ,  細孔径
準シソーラス用語： 腐食挙動 ,  表面形態 , 【Automatic Indexing@JST】

著者キーワード (6件)： マグネシウム ,  によるフッ素化 ,  耐食性 ,  ふっ化マグネシウム ,  生分解性 ,  プラズマ電解ふっ素化

分類 (1件)： 化成処理  (WC08050J)

タイトルに関連する用語 (7件)： 溶融 ,  アンモニウム ,  ふっ化水素 ,  陽極酸化 ,  生物医学 ,  マグネシウム合金 ,  分解