Effects of Mn Partitioning Temperature on Microstructure and Mechanical Properties of Low-Carbon Si-Mn Steel with I&Q&P Treatment

著者 (6件)： Chen Liansheng (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Dai Xin (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Song Jinying (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Tian Yaqiang (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Li Ran (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology) ,  Wei Yingli (Hebei Key Laboratory of Modern Metallurgy Technology,North China University of Science and Technology)
資料名： Jixie Gongcheng Cailiao  (Jixie Gongcheng Cailiao)
巻： 40  号： 11  ページ： 27-30  発行年： 2016年 
JST資料番号： C2051A  ISSN： 1000-3738  CODEN： JGCAEL  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 低鋼の微細構造と機械的性質に及ぼすMeng配分温度の影響を研究するために,低炭素鋼の種々の温度での二+++焼入れTan配分(I&Q&P)熱処理を実施した。結果は以下を示す。Meng配分の温度が上昇するにつれて,I&Q&P熱処理後のマルテンサイトの結晶粒は大きくなり,スラブの幅は増加し,スラブ間の距離は広くなった。試験鋼の伸びと残留オーステナイト含有量は最初に増加し,次に減少し,引張強さは直線的に減少した。800°Cにおいて,試験鋼の総合的性質は,最も高く,そして,強度は,29MPA MPAに達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： マルテンサイト ,  残留オーステナイト ,  低炭素鋼 ,  結晶粒 ,  引張強さ ,  焼入 ,  鋼 ,  *機械的性質 ,  熱処理 ,  伸び ,  微細構造

著者キーワード (5件)： Mn partitioning temperature ,  retained austenite ,  tensile strength ,  elongation ,  product of strength and ductility