固体酸化物燃料電池金属相互接続のためのCo40Mn/Co被覆の酸化挙動に及ぼすDyドーピングの役割【Powered by NICT】

The role of Dy doping on oxidation behavior of Co-40Mn/Co coating for solid oxide fuel cell metal interconnects

著者 (5件)： Lai Y.B. (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Jiangsu, 212003, China) ,  Guo P.Y. (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Jiangsu, 212003, China) ,  Shao Y. (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Jiangsu, 212003, China) ,  Zhang Y. (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Jiangsu, 212003, China) ,  Liu N. (School of Materials Science and Engineering, Jiangsu University of Science and Technology, Jiangsu, 212003, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 694  ページ： 383-393  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Co38Mn2DyとCo40Mn合金皮膜は高エネルギーマイクロアーク合金化(HEMAA)を用いて調製し,Co遷移層はまず304SSで得られた。調製および酸化後のCo-Mn(Dy)/Co被覆の微細構造と組成を,X線回折(XRD)と走査電子顕微鏡(SEM)により解析した。被覆は基板に金属学的結合をもつ飛沫出現と細粒構造である。Co-Mn被覆中のDyの添加は効果的に酸化物スケールの密着性を改善し,被覆の高温酸化速度を低下させることができる。基板からのFeおよびCrの外側への拡散は,Co38Mn2Dy/Co被覆のための外部酸化物層によって著しく抑制される。またDy酸化物,Mn酸化物と酸化物ペグは100hの酸化後の酸化物層であった。Coリッチ酸化物は高酸素分圧のためにトップスケール形成に有利であった。面積比抵抗(ASR)の値は800°CでCo38Mn2Dy/Co被覆の低いことを測定した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： クロム ,  走査電子顕微鏡 ,  密着性 ,  *酸化 ,  *被覆 ,  合金化 ,  高温酸化 ,  酸化マンガン ,  *マンガン ,  鉄 ,  X線回折 ,  *ジスプロシウム ,  *酸化物 ,  *相互接続
準シソーラス用語： 酸素分圧 , 【Automatic Indexing@JST】

著者キーワード (5件)： ジスプロシウム ,  Co40Mn/Co ,  被覆 ,  遷移層 ,  酸化

分類 (1件)： 金属系の相平衡・状態図  (CB03012T)

タイトルに関連する用語 (7件)： 固体酸化物燃料電池 ,  相互接続 ,  CO ,  酸化挙動 ,  Dy ,  ドーピング ,  役割