Preparation and performance of multi-armed and star-like poly(ethylene oxide)membrane for CO_2separation

著者 (6件)： Yang Pingping (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University) ,  Ding Xiaoli (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University) ,  Zhao Hongyong (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University) ,  Hua Mingming (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University) ,  Zhang Yuzhong (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University) ,  Wang Lina (Dalian Institute of Chemical Physics, Chinese Academy of Sciences)
資料名： Mokexue yu Jishu  (Mokexue yu Jishu)
巻： 36  号： 4  ページ： 14-18  発行年： 2016年 
JST資料番号： W1530A  ISSN： 1007-8924  CODEN： MKYJEF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 架橋剤として二重(に),架橋剤として二重(に),架橋剤として二重(ラジカル)を用いることにより,架橋ポリエチレンオキシドを調製した。膜の密度,ガラス転移温度,ガス透過性,およびガス透過性に及ぼす高分子組成の影響を研究した。結果は,ポリマー組成が密度にほとんど影響を及ぼさないことを示した。架橋剤含有量の増加と共に,高分子膜のガラス転移温度および熱伝導度は増加し,そして,高分子膜の拡散係数は減少し,そして,溶解度は,最初に減少して,次に増加し,そして,ガス透過性は減少した。調製した膜材料はCO_2に対して良好な浸透性があり、35°C、0.2MPAで、CO_2の浸透係数は1 110.89 BARRERに達し、CO_2/N_2とCO_2/CH_4の選択性はそれぞれ42.84%と13.30.%に達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 浸透率 ,  透気性 ,  熱伝導率 ,  *二酸化炭素 ,  高分子 ,  拡散係数 ,  ポリエチレンオキシド ,  重合体 ,  溶解度 ,  ガラス転移点 ,  高分子膜
準シソーラス用語： 浸透係数 , 【Automatic Indexing@JST】

著者キーワード (3件)： photopolymerization ,  CO_2separation membrane ,  PEO membrane

分類 (3件)： 膜分離  (XD02120Z) ,  高分子固体のその他の性質  (CG02025L) ,  物理的性質一般  (YH02021U)

タイトルに関連する用語 (4件)： 二酸化炭素 ,  酸化炭素 ,  調製 ,  研究