CaO B_2O_3SiO_2ガラス/CaTiO_3系に基づく中誘電率をもつLTCC組成の合成と特性化【Powered by NICT】

Synthesis and characterization of LTCC compositions with middle permittivity based on CaO-B₂O₃-SiO₂ glass/CaTiO₃ system

著者 (16件)： Ren Luchao (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Ren Luchao (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Luo Xianfu (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Luo Xianfu (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Hu Lisong (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Hu Lisong (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Sun Qinglei (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Sun Qinglei (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Xia Yunsheng (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Xia Yunsheng (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Hu Yongkang (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Hu Yongkang (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Gong Wenyuan (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Gong Wenyuan (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Zhou Hongqing (College of Materials Science and Engineering, Nanjing Tech University, Nanjing, Jiangsu, 210009, China) ,  Zhou Hongqing (Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing, Jiangsu, 210009, China)
資料名： Journal of the European Ceramic Society  (Journal of the European Ceramic Society)
巻： 37  号： 2  ページ： 619-623  発行年： 2017年 
JST資料番号： E0801B  ISSN： 0955-2219  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： CaO B_2O_3SiO_2(CBS)ガラス(45 55wt%)複合材料を添加したCaTiO_3セラミックスは830°C,850°C,875°Cと900°Cで焼結した。複合材料の性質に及ぼす異なるガラス含有量と焼結温度の影響機構を説明するために,異なる定性および定量的測定器を用いて複合材料の多重性能に焦点を当てた。875°Cで焼結した50wt%ガラスを有する複合材料は,かなり理想的な性能を示した:バルク密度は3.20g/~3であり,誘電率は25.7であった,誘電損失は7GHzで0.0009であった。複合材料の微細構造解析は,約1μmサイズのわずかな細孔以外の緻密で空孔のない微細構造を示した。加えて,複合材料はAg電極の収縮要求を満たすことができ,恐らくもはやAg電極と反応しなかった。は,低い焼結温度で様々な誘電体用途に適している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 容積重 ,  複合材料 ,  銀 ,  定性分析 ,  *ガラス ,  誘電損失 ,  *誘電率 ,  微細構造 ,  焼結 ,  多重度 ,  *キャラクタリゼーション ,  細孔
準シソーラス用語： 焼結温度 , 【Automatic Indexing@JST】

著者キーワード (5件)： CaTiO_3 ,  ガラスセラミック ,  誘電特性 ,  テープ鋳造 ,  LTCC応用