コンクリートの収縮亀裂の幾何学的特性とそれらの二次イオン浸透への影響【JST・京大機械翻訳】

Geometrical characteristic of concrete shrinkage crack and its effect on chloride ion permeability

著者 (7件)： Zhu Hongguang (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing)) ,  Yi Cheng (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing)) ,  Sun Fuyan (Huaneng Coal Industry Co., Ltd.) ,  Xie Yonglan (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing)) ,  Zhou Jiajie (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing)) ,  Wu Kaibo (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing)) ,  Liu Hong (School of Mechanics and Civil Engineering, China University of Mining and Technology(Beijing))
資料名： Harbin Gongye Daxue Xuebao  (Harbin Gongye Daxue Xuebao)
巻： 48  号： 12  ページ： 142-147  発行年： 2016年 
JST資料番号： W1450A  ISSN： 0367-6234  CODEN： HPKYAY  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 収縮亀裂の幾何学的特性を正確に表現し,コンクリート中の塩化物イオンの浸透法則に対する影響を解析するために,収縮亀裂の幾何学的特性を観察し統計的に解析し,コンクリートの塩化物イオン結果は以下を示す。その結果,コンクリートの収縮亀裂には顕著なアスペクト比があり,その平均値は約44.31であり,亀裂角度の平均値は約2.6度であることが分かった。最大幅,最小幅,平均幅,比表面積などの異なる亀裂幅の特性パラメータを比較することにより,亀裂幅が亀裂のコンクリートの透過性に及ぼす影響を評価する適切なパラメータであることを示した。亀裂コンクリート中の塩化物イオンの浸透係数は亀裂の最大幅と正の関係があり,収縮亀裂幅が0.18MMより小さい場合には,浸透係数に対する亀裂の影響は無視できる。収縮亀裂の幅の変化はコンクリートの不浸透性に著しく影響し、実際の工事ではコンクリートの保護層の厚さに従って、最大許容幅を確定すべきである。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 比表面積 ,  亀裂幅 ,  浸透率 ,  アスペクト比 ,  *亀裂 ,  *コンクリート ,  *浸透
準シソーラス用語： 保護層 ,  浸透係数 ,  透過性 ,  塩化物イオン ,  *収縮亀裂 , 【Automatic Indexing@JST】

著者キーワード (5件)： shrinkage crack ,  depth-to-width ratio ,  chloride ion permeability ,  crack tip angle ,  crack width