冷間圧延と変態区間焼なましにより作製した超微細粒二相鋼の集合組織発達に及ぼすNbの影響【Powered by NICT】

The effect of Nb on texture evolutions of the ultrafine-grained dual-phase steels fabricated by cold rolling and intercritical annealing

著者 (6件)： Ghatei Kalashami A. (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Kermanpur A. (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Ghassemali E. (Jonkoping University, School of Engineering, Department of Materials and Manufacturing, P.O. Box 1026, SE-551 11 Jonkoping, Sweden) ,  Najafizadeh A. (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Mazaheri Y. (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Mazaheri Y. (Department of Materials Engineering, Bu-Ali Sina University, Hamedan 65178-38695, Iran)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 694  ページ： 1026-1035  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 種々の量のNbの二相(DP)鋼は,フェライト-マルテンサイト二相初期組織の冷間圧延と変態区間焼なましを用いて作製した。ミクロ組織と集合組織変化に及ぼすNb含有量(0.00,0.06,0.12および0.18wt%)の影響を調べた。Nbの添加は約~1μmと均一分散マルテンサイト粒子のフェライト粒径の超微細結晶粒構造の形成を促進した。結果はNb含有量を有する微細構造の{111}繊維成分の高傾角粒界と形成の割合の増加を示した。さらに,テクスチャパワーはNbの添加で減少し,ランダム集合組織成分が得られた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微細構造 ,  *集合組織 ,  マルテンサイト ,  高傾角粒界 ,  *ニオブ ,  粒径 ,  *超微粒子 ,  *鋼 ,  微結晶 ,  *二相鋼 ,  フェライト ,  *冷間圧延
準シソーラス用語： EBSD ,  テクスチャ ,  *変態区間焼なまし , 【Automatic Indexing@JST】