非等温結晶化速度とCu-Zr-Alバルク金属ガラスの脆性に及ぼすイットリウム添加の影響【Powered by NICT】

Effect of yttrium addition on the non-isothermal crystallization kinetics and fragility of Cu-Zr-Al bulk metallic glass

著者 (5件)： Bing Li (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Yanhong Li (Shaanxi Key Laboratory for Photoelectric Functional Materials and Devices, Xi’an Technological University, Xi’an 710021, China) ,  Ke Yang (Shaanxi Key Laboratory for Photoelectric Functional Materials and Devices, Xi’an Technological University, Xi’an 710021, China) ,  Jinshan Li (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China) ,  Xinhui Fan (Shaanxi Key Laboratory for Photoelectric Functional Materials and Devices, Xi’an Technological University, Xi’an 710021, China)
資料名： Thermochimica Acta  (Thermochimica Acta)
巻： 642  ページ： 105-110  発行年： 2016年 
JST資料番号： E0350C  ISSN： 0040-6031  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Cu_43Zr_48Al_9と(Cu_43Zr_48Al_9)98Y_2の組成を有するバルク金属ガラスを銅鋳型鋳造法により作製した。X線回折(XRD)および示差走査熱量測定(DSC)を用いて,それらの構造と非等温結晶化速度論を調べた。結果は,結晶化に及ぼす加熱速度の影響はガラス転移上のそれよりも大きいことを示した。(Cu_43Zr_48Al_9)98Y_2の結晶化プロセスであるCu_43Zr_48Al_9のそれよりも加熱速度により敏感であった。イットリウム添加により,結晶化のガラス転移と核形成過程が容易になるが,結晶化の粒成長過程は活性化エネルギーに基づいて,より困難になる。(Cu_43Zr_48Al_9)98Y_2のAvrami指数は低い加熱速度,Cu_43Zr_48Al_9の場合と全く異なっているで減少した。これら二つのバルク金属ガラスは,脆弱性指標に従って「中間割れ易いガラス」として考慮すべきである。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *結晶化 ,  *脆性 ,  X線回折 ,  加熱速度 ,  *イットリウム ,  活性化エネルギー ,  示差走査熱量測定 ,  *ガラス ,  ガラス転移 ,  *銅 ,  速度論 ,  *バルク金属ガラス ,  晶析速度
準シソーラス用語： Avrami指数 ,  *非等温結晶化 , 【Automatic Indexing@JST】

著者キーワード (4件)： バルク金属ガラス ,  イットリウム添加 ,  結晶化速度論 ,  活性化エネルギー

分類 (2件)： 非晶質金属の構造  (BK04020D) ,  金属の結晶成長  (BK13030M)

タイトルに関連する用語 (7件)： 非等温結晶化 ,  Cu ,  Zr ,  Al ,  バルク金属ガラス ,  脆性 ,  イットリウム